WX07423H - X H
FOREVER
Product Description |
Our product is composed of 15% stainless steel fiber mixed with ABS material, resulting in a highly conductive and shielding product with excellent performance in terms of flame retardancy.
The presence of stainless steel fiber enhances the conductivity of the product, making it suitable for applications where electrical conductivity is required. The shielding capabilities of the product help to protect against electromagnetic interference (EMI) and radio frequency interference (RFI).
In addition to its conductive and shielding properties, our product also exhibits excellent wear resistance, making it ideal for use in healthcare settings where durability is essential. The high hardness of the material ensures that it can withstand repetitive use and maintain its structural integrity.
Furthermore, our product is designed with recyclability in mind, making it a sustainable choice for various applications. The recycling properties of the material allow for a reduced environmental impact and support the circular economy.
Overall, our PBT-based product offers a combination of conductivity, shielding, wear resistance, and recyclability that makes it suitable for a wide range of applications in industries such as electronics, healthcare, and manufacturing. |
General |
Form Resin Pellets |
Filler proprietary lubricants |
Feature Abrasion Resistant Internally Lubricated |
Uses Healthcare Packaging |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.4 g/cm³ ASTM D792 1.4 g/cm³ ISO 1183 |
Moisture Absorption(23 °C;50% RH/24 hrs) 0.07 % ASTM D570 |
Mold Shrinkage, Flow(24 hrs) 2.6 - 2.8 % ASTM D955 |
Mold Shrinkage, XFlow(24 hrs) 2.5 - 2.7 % ASTM D955 |
Melt Flow Rate[MFR](250 °C;5 kgf) 62 g/10min ASTM D1238 |
Wear Factor Washer 5 10^-10 in^5-min/ft-lb-hr ASTM D3702 |
Dynamic Cof 0.33 ASTM D3702 |
Static Cof 0.24 ASTM D3702 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 550 J/m | ASTM D4812 |
80*10*4;23 °C | 44 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 30 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
5 mm/min;Type I | 43 MPa | ASTM D638 |
5 mm/min | 45 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 43 MPa | ASTM D638 |
5 mm/min | 45 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 11 % | ASTM D638 |
5 mm/min | 17.8 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 14 % | ASTM D638 |
5 mm/min | 18.9 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2680 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 74 MPa | ASTM D790 |
2 mm/min | 74 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2300 MPa | ASTM D790 |
2 mm/min | 2400 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 55 °C | ASTM D648 |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 °C |
Drying Time<Injection> | 4 hrs |
Maximum Moisture Content<Injection> | 0.05 % |
Melt Temperature<Injection> | 240 - 265 °C |
Front, Zone 3 Temperature<Injection> | 260 - 270 °C |
Middle, Zone 2 Temperature<Injection> | 245 - 255 °C |
Rear, Zone 1 Temperature<Injection> | 220 - 230 °C |
Mold Temperature<Injection> | 80 - 100 °C |
Back Pressure<Injection> | 0.2 - 0.3 MPa |
Screw Speed <Injection> | 30 - 60 rpm |
Product Description |
Our product is composed of 15% stainless steel fiber mixed with ABS material, resulting in a highly conductive and shielding product with excellent performance in terms of flame retardancy.
The presence of stainless steel fiber enhances the conductivity of the product, making it suitable for applications where electrical conductivity is required. The shielding capabilities of the product help to protect against electromagnetic interference (EMI) and radio frequency interference (RFI).
In addition to its conductive and shielding properties, our product also exhibits excellent wear resistance, making it ideal for use in healthcare settings where durability is essential. The high hardness of the material ensures that it can withstand repetitive use and maintain its structural integrity.
Furthermore, our product is designed with recyclability in mind, making it a sustainable choice for various applications. The recycling properties of the material allow for a reduced environmental impact and support the circular economy.
Overall, our PBT-based product offers a combination of conductivity, shielding, wear resistance, and recyclability that makes it suitable for a wide range of applications in industries such as electronics, healthcare, and manufacturing. |
General |
Form Resin Pellets |
Filler proprietary lubricants |
Feature Abrasion Resistant Internally Lubricated |
Uses Healthcare Packaging |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.4 g/cm³ ASTM D792 1.4 g/cm³ ISO 1183 |
Moisture Absorption(23 °C;50% RH/24 hrs) 0.07 % ASTM D570 |
Mold Shrinkage, Flow(24 hrs) 2.6 - 2.8 % ASTM D955 |
Mold Shrinkage, XFlow(24 hrs) 2.5 - 2.7 % ASTM D955 |
Melt Flow Rate[MFR](250 °C;5 kgf) 62 g/10min ASTM D1238 |
Wear Factor Washer 5 10^-10 in^5-min/ft-lb-hr ASTM D3702 |
Dynamic Cof 0.33 ASTM D3702 |
Static Cof 0.24 ASTM D3702 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 550 J/m | ASTM D4812 |
80*10*4;23 °C | 44 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 30 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
5 mm/min;Type I | 43 MPa | ASTM D638 |
5 mm/min | 45 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 43 MPa | ASTM D638 |
5 mm/min | 45 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 11 % | ASTM D638 |
5 mm/min | 17.8 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 14 % | ASTM D638 |
5 mm/min | 18.9 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2680 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 74 MPa | ASTM D790 |
2 mm/min | 74 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2300 MPa | ASTM D790 |
2 mm/min | 2400 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 55 °C | ASTM D648 |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 °C |
Drying Time<Injection> | 4 hrs |
Maximum Moisture Content<Injection> | 0.05 % |
Melt Temperature<Injection> | 240 - 265 °C |
Front, Zone 3 Temperature<Injection> | 260 - 270 °C |
Middle, Zone 2 Temperature<Injection> | 245 - 255 °C |
Rear, Zone 1 Temperature<Injection> | 220 - 230 °C |
Mold Temperature<Injection> | 80 - 100 °C |
Back Pressure<Injection> | 0.2 - 0.3 MPa |
Screw Speed <Injection> | 30 - 60 rpm |