Product Description | ||||||
LUX2489D-XH is a high-quality polycarbonate resin suitable for injection molding applications. Featuring a medium viscosity and UV additive, this resin offers exceptional light reflection properties, making it ideal for applications where light transmission is important. Additionally, LUX2489D-XH has been formulated to exhibit low dust attraction, ensuring a clean and easy processing experience for manufacturers. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Feature | Outdoor | High Reflection | Low Dust Attraction | |||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity |
1.32 g/cm³ 1.32 g/cm³ |
ASTM D792 ISO 1183 | ||||
Moisture Absorption(50% RH;23 °C) | 0.150 % | ISO 62 | ||||
Water Absorption at Saturation | 0.35 % | ISO 62 | ||||
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm) | 0.5 - 0.7 % | |||||
Linear Mold Shrinkage, Transverse(Thickness; 3.2 mm) | 0.5 - 0.7 % | |||||
Melt Flow(1.2 kg;300 °C) | 13 g/10min | ASTM D1238 | ||||
Melt Volume Rate, MVR(1.2 kg;300 °C) | 13 cm³/10 min | ISO 1133 | ||||
Ball Indentation Hardness(H 358/30) | 95.0 MPa | ISO 2039-1 | ||||
Mechanical | Nominal Value | Test Method | ||||
Tensile Strength, Break 50 mm/min |
69.0 MPa 70.0 MPa |
ASTM D638-1 ISO 527 | ||||
Tensile Strength, Yield 50 mm/min |
62.0 MPa 63.0 MPa |
ASTM D638-1 ISO 527 | ||||
Elongation at Break
50 mm/min |
120 % 130 % |
ISO 527 ASTM D638-1 | ||||
Elongation at Yield
50 mm/min |
6.0 % 7.0 % |
ISO 527 ASTM D638-1 | ||||
Tensile Modulus |
2300 MPa 2350 MPa |
ASTM D638 ISO 527 | ||||
Flexural Yield Strength
1.3 mm/min;50 mm;span |
90.0 MPa 97.0 MPa |
ISO 178 ASTM D790 | ||||
Flexural Modulus
1.3 mm/min;50 mm;span |
2300 MPa 2340 MPa |
ISO 178 ASTM D790 | ||||
Izod Impact, Notched Temperature; 23 °C Temperature; -30 °C |
801 J/m 125 J/m | ASTM D256 | ||||
Izod Impact, Notched, ISO Temperature; 23 °C;80x10x3 mm Temperature; -30 °C;80x10x3 mm |
65.0 kJ/m² 12.0 kJ/m² | ISO 180/1A | ||||
Izod Impact, Unnotched, ISO Temperature; 23 °C;80x10x3 mm Temperature; -30 °C;80x10x3 mm |
No Break No Break | ISO 180/1eU | ||||
Charpy Impact Unnotched Temperature; 23 °C Temperature; -30 °C |
No Break No Break | ISO 179 1eU | ||||
Charpy Impact, Notched Temperature; 23 °C Temperature; -30 °C |
73 kJ/m² 14 kJ/m² | ISO 179 1eA | ||||
Dart Drop, Total Energy(Temperature; 23 °C) | 64.0 J | ASTM D3763 | ||||
Taber Abrasion, mg/1000 Cycles(1.0e+3 Cycles;CS-17 Wheel;1kg) | 10 mg | SABIC Method |
Thermal | Nominal Value | Test Method |
CTE, Flow 23 - 80 °C Temperature; -40 - 40 °C |
70.0 µm/m-°C 70.0 µm/m-°C |
ISO 11359-2 ASTM E831 |
CLTE, Transverse 23 - 80 °C Temperature; -40 - 40 °C |
70.0 µm/m-°C 70.0 µm/m-°C |
ISO 11359-2 ASTM E831 |
Thermal Conductivity | 0.200 W/m-K | ISO 8302 |
Deflection Temperature | ||
Pressure; 0.46 MPa;Edgew;120*10*4;sp=100mm 0 | 135 °C | ISO 75/Be |
Pressure; 1.8 MPa;Edgew;120*10*4;sp=100mm 0 | 123 °C | ISO 75/Ae |
Thickness; 3.2 mm;Pressure; 1.8 MPa | 114 °C | ASTM D648 |
Thickness; 6.4 mm;Pressure; 1.8 MPa | 130 °C | ASTM D648 |
Vicat Softening Point | ||
Rate B/50 | 140 °C | ISO 306 |
Rate B/120 | 141 °C | ISO 306 |
Rate B/50 | 153 °C | ASTM D1525 |
Glow Wire Test(Thickness; 1.6 mm) | 850 °C | IEC 60695-2-12 |
Electrical | Nominal Value | Test Method |
Surface Resistance | 5.00e+13 Ohms | ASTM D257 |
Optical | Nominal Value | Test Method |
Refractive Index | 1.586 | ISO 489 |
1 What is the reflector cup in the led lamps?
The reflector is for long-distance spotlighting, and its appearance is cup-shaped. It can use limited light energy to control the illumination distance and illumination area of the main spot.
Product Description | ||||||
LUX2489D-XH is a high-quality polycarbonate resin suitable for injection molding applications. Featuring a medium viscosity and UV additive, this resin offers exceptional light reflection properties, making it ideal for applications where light transmission is important. Additionally, LUX2489D-XH has been formulated to exhibit low dust attraction, ensuring a clean and easy processing experience for manufacturers. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Feature | Outdoor | High Reflection | Low Dust Attraction | |||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity |
1.32 g/cm³ 1.32 g/cm³ |
ASTM D792 ISO 1183 | ||||
Moisture Absorption(50% RH;23 °C) | 0.150 % | ISO 62 | ||||
Water Absorption at Saturation | 0.35 % | ISO 62 | ||||
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm) | 0.5 - 0.7 % | |||||
Linear Mold Shrinkage, Transverse(Thickness; 3.2 mm) | 0.5 - 0.7 % | |||||
Melt Flow(1.2 kg;300 °C) | 13 g/10min | ASTM D1238 | ||||
Melt Volume Rate, MVR(1.2 kg;300 °C) | 13 cm³/10 min | ISO 1133 | ||||
Ball Indentation Hardness(H 358/30) | 95.0 MPa | ISO 2039-1 | ||||
Mechanical | Nominal Value | Test Method | ||||
Tensile Strength, Break 50 mm/min |
69.0 MPa 70.0 MPa |
ASTM D638-1 ISO 527 | ||||
Tensile Strength, Yield 50 mm/min |
62.0 MPa 63.0 MPa |
ASTM D638-1 ISO 527 | ||||
Elongation at Break
50 mm/min |
120 % 130 % |
ISO 527 ASTM D638-1 | ||||
Elongation at Yield
50 mm/min |
6.0 % 7.0 % |
ISO 527 ASTM D638-1 | ||||
Tensile Modulus |
2300 MPa 2350 MPa |
ASTM D638 ISO 527 | ||||
Flexural Yield Strength
1.3 mm/min;50 mm;span |
90.0 MPa 97.0 MPa |
ISO 178 ASTM D790 | ||||
Flexural Modulus
1.3 mm/min;50 mm;span |
2300 MPa 2340 MPa |
ISO 178 ASTM D790 | ||||
Izod Impact, Notched Temperature; 23 °C Temperature; -30 °C |
801 J/m 125 J/m | ASTM D256 | ||||
Izod Impact, Notched, ISO Temperature; 23 °C;80x10x3 mm Temperature; -30 °C;80x10x3 mm |
65.0 kJ/m² 12.0 kJ/m² | ISO 180/1A | ||||
Izod Impact, Unnotched, ISO Temperature; 23 °C;80x10x3 mm Temperature; -30 °C;80x10x3 mm |
No Break No Break | ISO 180/1eU | ||||
Charpy Impact Unnotched Temperature; 23 °C Temperature; -30 °C |
No Break No Break | ISO 179 1eU | ||||
Charpy Impact, Notched Temperature; 23 °C Temperature; -30 °C |
73 kJ/m² 14 kJ/m² | ISO 179 1eA | ||||
Dart Drop, Total Energy(Temperature; 23 °C) | 64.0 J | ASTM D3763 | ||||
Taber Abrasion, mg/1000 Cycles(1.0e+3 Cycles;CS-17 Wheel;1kg) | 10 mg | SABIC Method |
Thermal | Nominal Value | Test Method |
CTE, Flow 23 - 80 °C Temperature; -40 - 40 °C |
70.0 µm/m-°C 70.0 µm/m-°C |
ISO 11359-2 ASTM E831 |
CLTE, Transverse 23 - 80 °C Temperature; -40 - 40 °C |
70.0 µm/m-°C 70.0 µm/m-°C |
ISO 11359-2 ASTM E831 |
Thermal Conductivity | 0.200 W/m-K | ISO 8302 |
Deflection Temperature | ||
Pressure; 0.46 MPa;Edgew;120*10*4;sp=100mm 0 | 135 °C | ISO 75/Be |
Pressure; 1.8 MPa;Edgew;120*10*4;sp=100mm 0 | 123 °C | ISO 75/Ae |
Thickness; 3.2 mm;Pressure; 1.8 MPa | 114 °C | ASTM D648 |
Thickness; 6.4 mm;Pressure; 1.8 MPa | 130 °C | ASTM D648 |
Vicat Softening Point | ||
Rate B/50 | 140 °C | ISO 306 |
Rate B/120 | 141 °C | ISO 306 |
Rate B/50 | 153 °C | ASTM D1525 |
Glow Wire Test(Thickness; 1.6 mm) | 850 °C | IEC 60695-2-12 |
Electrical | Nominal Value | Test Method |
Surface Resistance | 5.00e+13 Ohms | ASTM D257 |
Optical | Nominal Value | Test Method |
Refractive Index | 1.586 | ISO 489 |