Product Description | |||
Forever Polycarbonate Granules is an exceptional injection molding grade with a high flow and impact modification that has been UV-stabilized for long-lasting durability. It has been formulated with a non-bromine, non-chlorine flame retardant system to provide excellent fire resistance and offers UL94 V0 @ 1.5mm flame retardancy. These granules have low-temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC for the utmost efficiency in manufacturing. Polycarbonate resin is available in a vast array of opaque colors, making it suitable for a broad range of applications. Forever Polycarbonate Granules to exceed your expectations for quality and performance. | |||
General | |||
Form | Resin Pellets | ||
Non-Chlorinated Excellent Processability Non-Brominated | |||
Feature Low Temperature Impact F1 High Impact | |||
Easy Process | |||
Battery Cases Rail PV Convertor Box Energy Storage | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2050 MPa | ASTM D638 | |
Tensile Strength, Break 60.0 MPa ASTM D638 | |||
Tensile Elongation, Break 108 % ASTM D638 | |||
Flexural Modulus 2400 MPa ASTM D790 | |||
Flexural Strength 88.0 MPa ASTM D790 | |||
Notched Izod Impact | ASTM D256 | ||
-30 °C | 620 J/m | ||
23 °C | 750 J/m |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa;3 2 mm) | 120°C | ASTM D648 |
Flame Rating 1.5 mm 3 mm | V-0 5VA | UL 94 |
Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 270 - 295 °C | |
Middle Temperature<injection> | 280 - 305 °C | |
Front Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Processing Temp, Melt<Injection> | 295 - 315 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
1 What the technical data sheet of the PC resins or granules?
Product Description | |||
Forever Polycarbonate Granules is an exceptional injection molding grade with a high flow and impact modification that has been UV-stabilized for long-lasting durability. It has been formulated with a non-bromine, non-chlorine flame retardant system to provide excellent fire resistance and offers UL94 V0 @ 1.5mm flame retardancy. These granules have low-temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC for the utmost efficiency in manufacturing. Polycarbonate resin is available in a vast array of opaque colors, making it suitable for a broad range of applications. Forever Polycarbonate Granules to exceed your expectations for quality and performance. | |||
General | |||
Form | Resin Pellets | ||
Non-Chlorinated Excellent Processability Non-Brominated | |||
Feature Low Temperature Impact F1 High Impact | |||
Easy Process | |||
Battery Cases Rail PV Convertor Box Energy Storage | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2050 MPa | ASTM D638 | |
Tensile Strength, Break 60.0 MPa ASTM D638 | |||
Tensile Elongation, Break 108 % ASTM D638 | |||
Flexural Modulus 2400 MPa ASTM D790 | |||
Flexural Strength 88.0 MPa ASTM D790 | |||
Notched Izod Impact | ASTM D256 | ||
-30 °C | 620 J/m | ||
23 °C | 750 J/m |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa;3 2 mm) | 120°C | ASTM D648 |
Flame Rating 1.5 mm 3 mm | V-0 5VA | UL 94 |
Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 270 - 295 °C | |
Middle Temperature<injection> | 280 - 305 °C | |
Front Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Processing Temp, Melt<Injection> | 295 - 315 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Vent Depth<Injection> | 0.025 - 0.076 mm |