PX11311U-XH
Forever
PX11311U-XH is a compound that is made from Nylon 6 resin mixed with mineral and glass fiber. This grade of compound has several additional properties, including being able to conduct heat, insulate electricity, withstand UV radiation better, and being flame retardant without the use of bromine or chlorine.
General | |||||
Form | Resin Pellets | ||||
Filler | Glass Fiber | Mineral | |||
Feature | Thermally Conductive Non-Chlorinated | Outdoor Electrically Isolative | Non-Brominated & Non- Chlorinated Flame Retardant | ||
Usage: Industria | Electrical | Building and Construction | |||
Physical | Nominal Value | Test Method | |||
Mold Shrinkage, Flow(24 hrs) | 0.45 % | ISO 294 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.65 % | ISO 294 | |||
Density / Specific Gravity | 1.74 g/cm³ | ISO 1183 | |||
Water Absorption(24 hrs;23 °C) | 0.36 % | ISO 62-1 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched(80*10*4;23 °C) | 25 kJ/m² | ISO 180/1U | |||
Izod Impact, Notched(80*10*4;23 °C) | 3 kJ/m² | ISO 180/1A | |||
Tensile Stress, Break(5 mm/min) | 105 MPa | ISO 527 | |||
Tensile Strain, Break(5 mm/min) | 1.7 % | ISO 527 | |||
Tensile Modulus(1 mm/min) | 1.2E+04 MPa | ISO 527 | |||
Flexural Stress, Yield(2 mm/min) | 170 MPa | ISO 178 | |||
Flexural Modulus(2 mm/min) | 1.1E+04 MPa | ISO 178 | |||
Thermal | Nominal Value | Test Method | |||
UL Recognized(≥ 1 mm) | V-0 | UL 94 | |||
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 1.6 mm 3 mm |
800 °C 775 °C 775 °C 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 1 mm |
960 °C 960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 209 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
3.1E-05 1/°C 3.5e-05 1/°C 3.7E-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
4.8E-05 1/°C 6.0E-05 1/°C 7.3e-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
Thermal conductivity through plane 60*60*3mm plaque ?80*3mm discs |
0.8 W/m-K 1.1 W/m-K | ISO 22007-2 |
Thermal conductivity in plane 60*60*3mm plaque ?80*3mm discs |
1.5 W/m-K 1.3 W/m-K | ISO 22007-2 |
Ball Pressure Test 125°C +/- 2°C 165°C +/- 2°C |
PASSES PASSES | IEC 60695-10-2 |
Vicat Softening Temperature(Rate B/120) | 205 °C | ISO 306 |
HDT/Bf(0.45) | 208 °C | ISO 75/Bf |
HDT/Af(1.8) | 185 °C | ISO 75/Af |
Relative Temp Index, Elec | 120 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 110 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+16 ohms | ASTM D257 |
Dielectric Strength, in Oil(1.6 mm) | 15.9 kV/mm | ASTM D149 |
Comparative Tracking Index, CTI | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI( ≥ 1 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 1 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 20 - 60 rpm |
PX11311U-XH is a compound that is made from Nylon 6 resin mixed with mineral and glass fiber. This grade of compound has several additional properties, including being able to conduct heat, insulate electricity, withstand UV radiation better, and being flame retardant without the use of bromine or chlorine.
General | |||||
Form | Resin Pellets | ||||
Filler | Glass Fiber | Mineral | |||
Feature | Thermally Conductive Non-Chlorinated | Outdoor Electrically Isolative | Non-Brominated & Non- Chlorinated Flame Retardant | ||
Usage: Industria | Electrical | Building and Construction | |||
Physical | Nominal Value | Test Method | |||
Mold Shrinkage, Flow(24 hrs) | 0.45 % | ISO 294 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.65 % | ISO 294 | |||
Density / Specific Gravity | 1.74 g/cm³ | ISO 1183 | |||
Water Absorption(24 hrs;23 °C) | 0.36 % | ISO 62-1 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched(80*10*4;23 °C) | 25 kJ/m² | ISO 180/1U | |||
Izod Impact, Notched(80*10*4;23 °C) | 3 kJ/m² | ISO 180/1A | |||
Tensile Stress, Break(5 mm/min) | 105 MPa | ISO 527 | |||
Tensile Strain, Break(5 mm/min) | 1.7 % | ISO 527 | |||
Tensile Modulus(1 mm/min) | 1.2E+04 MPa | ISO 527 | |||
Flexural Stress, Yield(2 mm/min) | 170 MPa | ISO 178 | |||
Flexural Modulus(2 mm/min) | 1.1E+04 MPa | ISO 178 | |||
Thermal | Nominal Value | Test Method | |||
UL Recognized(≥ 1 mm) | V-0 | UL 94 | |||
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 1.6 mm 3 mm |
800 °C 775 °C 775 °C 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 1 mm |
960 °C 960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 209 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
3.1E-05 1/°C 3.5e-05 1/°C 3.7E-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
4.8E-05 1/°C 6.0E-05 1/°C 7.3e-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
Thermal conductivity through plane 60*60*3mm plaque ?80*3mm discs |
0.8 W/m-K 1.1 W/m-K | ISO 22007-2 |
Thermal conductivity in plane 60*60*3mm plaque ?80*3mm discs |
1.5 W/m-K 1.3 W/m-K | ISO 22007-2 |
Ball Pressure Test 125°C +/- 2°C 165°C +/- 2°C |
PASSES PASSES | IEC 60695-10-2 |
Vicat Softening Temperature(Rate B/120) | 205 °C | ISO 306 |
HDT/Bf(0.45) | 208 °C | ISO 75/Bf |
HDT/Af(1.8) | 185 °C | ISO 75/Af |
Relative Temp Index, Elec | 120 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 110 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+16 ohms | ASTM D257 |
Dielectric Strength, in Oil(1.6 mm) | 15.9 kV/mm | ASTM D149 |
Comparative Tracking Index, CTI | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI( ≥ 1 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 1 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 20 - 60 rpm |