Reinforced Polypropylene with 40% Long Glass Fibers Heat Stabilized PP Resin Particles for Automotive Applications. High Strength and Stiffness, Heat Resistant. Increased Notched Impact Strength at Various Temperatures. Reduced Creep and Minimized Warpage. Isotropic Shrinkage and High Reproducibility in Injection Molding.
General | ||
Form Resin Pellets | ||
Filler 40 % Long Glass Fiber | ||
Low Warpage | Creep Resistance | Good Thermal |
Features Good Hardness | Low Temperature Impact | Chemically Coupled |
Good Dimensional | ||
Usage Automotive | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.22 g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 9200 MPa | ISO 527-2/1A |
Tensile Stress, Break | 130 MPa | ISO 527-2/1A/5 |
Tensile Strain, Break | 2.0 % | ISO 527-2/1A/5 |
Flexural Modulus(23 °C) | 8200 MPa | ISO 178 |
Flexural Stress(23 °C) | 185 MPa | ISO 178 |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 30 kJ/m² | |
23 °C | 22 kJ/m² | |
C harpy Unnotched Impact Strength | ISO 179 1eU | |
-30 °C | 58 kJ/m² | |
23 °C | 62 kJ/m² | |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed | ||
1.8 MPa | 157 °C | ISO 75-2/A |
8 MPa | 134 °C | ISO 75-2/C |
Melting Point(10 °C/min) | 166 °C | ISO 11357-3 |
Processing | Nominal Value |
Drying Temperature<Injection> | 90 - 100 °C |
Drying Time<Injection> | 2.0 hr |
Suggested Max Moisture<Injection> | 0.20 % |
Rear Temperature<Injection> | 220 - 230 °C |
Middle Temperature<injection> | 230 - 240 °C |
Front Temperature<Injection> | 240 - 250 °C |
Nozzle Temperature<Injection> | 240 - 250 °C |
Processing Temp, Melt<Injection> | 230 - 270 °C |
Mold Temperature<Injection> | 40 - 70 °C |
Injection Rate<Injection> | Slow |
Back Pressure<Injection> | < 3.00 MPa |
Feeding Zone Temperature<Injection> | 20 - 50 °C |
Zone4 temperature<Injection> | 250 - 260 °C |
Hot Runner Temperature<Injection> | 230 - 270 °C |
Reinforced Polypropylene with 40% Long Glass Fibers Heat Stabilized PP Resin Particles for Automotive Applications. High Strength and Stiffness, Heat Resistant. Increased Notched Impact Strength at Various Temperatures. Reduced Creep and Minimized Warpage. Isotropic Shrinkage and High Reproducibility in Injection Molding.
General | ||
Form Resin Pellets | ||
Filler 40 % Long Glass Fiber | ||
Low Warpage | Creep Resistance | Good Thermal |
Features Good Hardness | Low Temperature Impact | Chemically Coupled |
Good Dimensional | ||
Usage Automotive | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.22 g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 9200 MPa | ISO 527-2/1A |
Tensile Stress, Break | 130 MPa | ISO 527-2/1A/5 |
Tensile Strain, Break | 2.0 % | ISO 527-2/1A/5 |
Flexural Modulus(23 °C) | 8200 MPa | ISO 178 |
Flexural Stress(23 °C) | 185 MPa | ISO 178 |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 30 kJ/m² | |
23 °C | 22 kJ/m² | |
C harpy Unnotched Impact Strength | ISO 179 1eU | |
-30 °C | 58 kJ/m² | |
23 °C | 62 kJ/m² | |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed | ||
1.8 MPa | 157 °C | ISO 75-2/A |
8 MPa | 134 °C | ISO 75-2/C |
Melting Point(10 °C/min) | 166 °C | ISO 11357-3 |
Processing | Nominal Value |
Drying Temperature<Injection> | 90 - 100 °C |
Drying Time<Injection> | 2.0 hr |
Suggested Max Moisture<Injection> | 0.20 % |
Rear Temperature<Injection> | 220 - 230 °C |
Middle Temperature<injection> | 230 - 240 °C |
Front Temperature<Injection> | 240 - 250 °C |
Nozzle Temperature<Injection> | 240 - 250 °C |
Processing Temp, Melt<Injection> | 230 - 270 °C |
Mold Temperature<Injection> | 40 - 70 °C |
Injection Rate<Injection> | Slow |
Back Pressure<Injection> | < 3.00 MPa |
Feeding Zone Temperature<Injection> | 20 - 50 °C |
Zone4 temperature<Injection> | 250 - 260 °C |
Hot Runner Temperature<Injection> | 230 - 270 °C |