DX14354X-XH
Forever
The DX14354X-XH compound is a specialized blend made from Polycarbonate (PC) resin mixed with exclusive additives. This grade offers various enhancements, such as improved plating surface and mechanical performance, making it ideal for Laser Direct Structuring (LDS) applications. It also exhibits improved flow, superior impact resistance, and the ability to be colored. Additionally, it is non-brominated and non-chlorinated, ensuring flame retardant properties.
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | High Impact | Non-Brominated & Non- Chlorinated Flame | |
Non-Chlorinated | Enhanced Ductility | Colorable | ||
Circuit Solution | Lds | Good Surface Appearance | ||
Uses | Automotive Electrical | Consumer Laser Direct Structuring | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.29 g/cm³ | ASTM D792 | ||
Mold Shrinkage, Flow(24 hrs) | 0.5 - 0.7 % | ASTM D955 | ||
Mold Shrinkage, XFlow(24 hrs) | 0.5 - 0.7 % | ASTM D955 | ||
Moisture Absorption(50% RH;23 °C) | 0.05 % | ISO 62 | ||
Melt Volume Rate, MVR | ISO 1133 | |||
5 kg;MVR at 260 °C | 25 cm³/10 min | |||
2.16 kg;MVR at 280 °C | 27 cm³/10 min | |||
21.6 kg;MVR at 280 °C | 22 cm³/10 min |
Mechanical | Nominal Value | Test Method |
Tensile Strain, Break | ||
50 mm/min;Type I | 70 % | ASTM D638 |
50 mm/min;Type I | 70 % | ASTM D638 |
50 mm/min | 80 % | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 44 MPa | ASTM D638 |
50 mm/min;Type I | 49 MPa | ASTM D638 |
50 mm/min | 47 MPa | ISO 527 |
Izod Impact, Notched(23 °C) | 750 J/m | ASTM D256 |
Izod impact strength, Notched(80*10*3;23 °C;23 °C) | 60 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
50 mm/min;Type I | 54 MPa | ASTM D638 |
50 mm/min | 54 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 5 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2500 MPa | ASTM D638 |
1 mm/min | 2460 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 85 MPa | ASTM D790 |
2 mm/min | 86 MPa | ISO 178 |
Flexural Stress, break(1.3 mm/min;50 mm;span) | 83 MPa | ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2500 MPa | ASTM D790 |
2 mm/min | 2560 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 1 mm) | V-1 | UL 94 |
Vicat Softening Temperature Rate A/50 Rate B/50 |
128 °C 128 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 111 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 5.7E-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 6.0E-05 1/°C | ASTM E831 |
HDT/Af(1.8) | 113 °C | ISO 75/Af |
Relative Temp Index, Elec | 80 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.2E+16 ohms ·cm | ASTM D257 |
Surface Resistivity | 1.2E+16 ohms | ASTM D257 |
Relative Permittivity(1.0e+9 Hz) | 3.1 | ASTM D150 |
Dissipation Factor 1.0e+9 Hz
|
6.0E-03
|
ASTM D150
|
Processing | Nominal Value |
Drying Temperature<Injection> | 110 - 120 °C |
Drying Time<Injection> | 2 - 4 hrs |
Maximum Moisture Content<Injection> | 0.02 % |
Melt Temperature<Injection> | 250 - 270 °C |
Nozzle Temperature<Injection> | 240 - 260 °C |
Front, Zone 3 Temperature<Injection> | 245 - 265 °C |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C |
Rear, Zone 1 Temperature<Injection> | 230 - 245 °C |
Hopper Temperature<Injection> | 40 - 60 °C |
Mold Temperature<Injection> | 40 - 100 °C |
The DX14354X-XH compound is a specialized blend made from Polycarbonate (PC) resin mixed with exclusive additives. This grade offers various enhancements, such as improved plating surface and mechanical performance, making it ideal for Laser Direct Structuring (LDS) applications. It also exhibits improved flow, superior impact resistance, and the ability to be colored. Additionally, it is non-brominated and non-chlorinated, ensuring flame retardant properties.
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | High Impact | Non-Brominated & Non- Chlorinated Flame | |
Non-Chlorinated | Enhanced Ductility | Colorable | ||
Circuit Solution | Lds | Good Surface Appearance | ||
Uses | Automotive Electrical | Consumer Laser Direct Structuring | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.29 g/cm³ | ASTM D792 | ||
Mold Shrinkage, Flow(24 hrs) | 0.5 - 0.7 % | ASTM D955 | ||
Mold Shrinkage, XFlow(24 hrs) | 0.5 - 0.7 % | ASTM D955 | ||
Moisture Absorption(50% RH;23 °C) | 0.05 % | ISO 62 | ||
Melt Volume Rate, MVR | ISO 1133 | |||
5 kg;MVR at 260 °C | 25 cm³/10 min | |||
2.16 kg;MVR at 280 °C | 27 cm³/10 min | |||
21.6 kg;MVR at 280 °C | 22 cm³/10 min |
Mechanical | Nominal Value | Test Method |
Tensile Strain, Break | ||
50 mm/min;Type I | 70 % | ASTM D638 |
50 mm/min;Type I | 70 % | ASTM D638 |
50 mm/min | 80 % | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 44 MPa | ASTM D638 |
50 mm/min;Type I | 49 MPa | ASTM D638 |
50 mm/min | 47 MPa | ISO 527 |
Izod Impact, Notched(23 °C) | 750 J/m | ASTM D256 |
Izod impact strength, Notched(80*10*3;23 °C;23 °C) | 60 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
50 mm/min;Type I | 54 MPa | ASTM D638 |
50 mm/min | 54 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 5 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2500 MPa | ASTM D638 |
1 mm/min | 2460 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 85 MPa | ASTM D790 |
2 mm/min | 86 MPa | ISO 178 |
Flexural Stress, break(1.3 mm/min;50 mm;span) | 83 MPa | ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2500 MPa | ASTM D790 |
2 mm/min | 2560 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 1 mm) | V-1 | UL 94 |
Vicat Softening Temperature Rate A/50 Rate B/50 |
128 °C 128 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 111 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 5.7E-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 6.0E-05 1/°C | ASTM E831 |
HDT/Af(1.8) | 113 °C | ISO 75/Af |
Relative Temp Index, Elec | 80 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.2E+16 ohms ·cm | ASTM D257 |
Surface Resistivity | 1.2E+16 ohms | ASTM D257 |
Relative Permittivity(1.0e+9 Hz) | 3.1 | ASTM D150 |
Dissipation Factor 1.0e+9 Hz
|
6.0E-03
|
ASTM D150
|
Processing | Nominal Value |
Drying Temperature<Injection> | 110 - 120 °C |
Drying Time<Injection> | 2 - 4 hrs |
Maximum Moisture Content<Injection> | 0.02 % |
Melt Temperature<Injection> | 250 - 270 °C |
Nozzle Temperature<Injection> | 240 - 260 °C |
Front, Zone 3 Temperature<Injection> | 245 - 265 °C |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C |
Rear, Zone 1 Temperature<Injection> | 230 - 245 °C |
Hopper Temperature<Injection> | 40 - 60 °C |
Mold Temperature<Injection> | 40 - 100 °C |