PP-GF30-02 AD 3019-XH
Forever
PP-GF30-02 AD 3019-XH is a 30% long glass fiber reinforced polypropylene with UV stability, commonly used as a plastic raw material for outdoor equipment.
General |
Form Resin Pellets |
Filler 30 % Long Glass Fiber |
Feature Outdoor |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.12 g/cm³ ISO 1183 |
Mechanical Nominal Value Test Method |
Tensile Modulus 6550 MPa ISO 527-2/1A |
Tensile Stress, Break 100 MPa ISO 527-2/1A/5 |
Tensile Strain, Break 2.1 % ISO 527-2/1A/5 |
Flexural Modulus(23 °C) 6500 MPa ISO 178 |
Flexural Stress(23 °C) 170 MPa ISO 178 |
C harpy Notched Impact Strength(23 °C) 19 kJ/m² ISO 179 1eA |
Thermal Nominal Value Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) 157 °C ISO 75-2/A |
Processing Nominal Value |
Drying Temperature<Injection> 90 - 100 °C |
Drying Time<Injection> 2.0 hr |
Suggested Max Moisture<Injection> 0.20 % |
Rear Temperature<Injection> 200 - 210 °C |
Middle Temperature<injection> 210 - 220 °C |
Front Temperature<Injection> 220 - 230 °C |
Nozzle Temperature<Injection> 230 - 240 °C |
Processing Temp, Melt<Injection> 230 - 240 °C |
Mold Temperature<Injection> 40 - 70 °C |
Feeding Zone Temperature<Injection> 20 - 50 °C |
Zone4 temperature<Injection> 230 - 240 °C |
PP-GF30-02 AD 3019-XH is a 30% long glass fiber reinforced polypropylene with UV stability, commonly used as a plastic raw material for outdoor equipment.
General |
Form Resin Pellets |
Filler 30 % Long Glass Fiber |
Feature Outdoor |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.12 g/cm³ ISO 1183 |
Mechanical Nominal Value Test Method |
Tensile Modulus 6550 MPa ISO 527-2/1A |
Tensile Stress, Break 100 MPa ISO 527-2/1A/5 |
Tensile Strain, Break 2.1 % ISO 527-2/1A/5 |
Flexural Modulus(23 °C) 6500 MPa ISO 178 |
Flexural Stress(23 °C) 170 MPa ISO 178 |
C harpy Notched Impact Strength(23 °C) 19 kJ/m² ISO 179 1eA |
Thermal Nominal Value Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) 157 °C ISO 75-2/A |
Processing Nominal Value |
Drying Temperature<Injection> 90 - 100 °C |
Drying Time<Injection> 2.0 hr |
Suggested Max Moisture<Injection> 0.20 % |
Rear Temperature<Injection> 200 - 210 °C |
Middle Temperature<injection> 210 - 220 °C |
Front Temperature<Injection> 220 - 230 °C |
Nozzle Temperature<Injection> 230 - 240 °C |
Processing Temp, Melt<Injection> 230 - 240 °C |
Mold Temperature<Injection> 40 - 70 °C |
Feeding Zone Temperature<Injection> 20 - 50 °C |
Zone4 temperature<Injection> 230 - 240 °C |