PP is reinforced by glass fiber, tensile strength reaches 65MPa~90MPa, bending strength reaches 70MPa~120MPa, bending modulus reaches 3000MPa~4500MPa, such mechanical strength is fully comparable with ABS and reinforced ABS products, and more heat resistant. The heat resistance temperature of glass fiber reinforced PP material can reach 135℃~145℃.
Technical Data Sheet | Glass Fiber Enhanced Items | Standard | Flame Retardant With Glass Fiber | Toughening | |||||
Items | Method | Unite | 800G15 | 800G20 | 800G30 | 800G40 | 800 | 800G20-V15 | 800ST |
Physical Property | |||||||||
Specific Gravity | ASTM D792 | − | 1.01 | 1.05 | 1.12 | 1.22 | 0.91 | 1.22 | 0.9 |
Water Absorption | ASTM D570 | % | 0.05 | 0.05 | 0.04 | 0.03 | 0.06 | 0.05 | 0.07 |
Molding Shrinkage | ASTM D955 | % | 0.6-1.0 | 0.6-1.0 | 0.6-0.8 | 0.3-0.7 | 1.6-1.8 | 0.5-0.7 | 1.3-2.0 |
Melt Flow Index(200℃,10kg) | ASTM 1238 | g/10min | 6.5 | 4 | 3 | 3 | 7 | 4 | 5 |
Glass Fiber Content | − | % | 15 | 20 | 30 | 40 | − | 20 | − |
Mechanical Property | |||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 65 | 78 | 90 | 32 | 55 | 20 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 5 | 5.5 | 3.6 | 3 | 300 | 5 | >300 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 95 | 120 | 145 | 52 | 70 | 25 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2400 | 3200 | 4100 | 6400 | 1240 | 3000 | 800 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 10 | 11 | 13 | 13 | 5 | 4 | 680 |
Thermal Property | |||||||||
Heat Deflection Temperature(0.45MPa) | ASTM D648 | ℃ | 145 | 145 | 155 | 157 | 124 | 148 | 118 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB |
Electrical Property | |||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||
CTI(23℃) | IEC60112 | V | |||||||
Surface Resistivity | IEC 60093 | Ω | |||||||
Volume Resistivity | ICE 60093 | Ω.cm |
PP is reinforced by glass fiber, tensile strength reaches 65MPa~90MPa, bending strength reaches 70MPa~120MPa, bending modulus reaches 3000MPa~4500MPa, such mechanical strength is fully comparable with ABS and reinforced ABS products, and more heat resistant. The heat resistance temperature of glass fiber reinforced PP material can reach 135℃~145℃.
Technical Data Sheet | Glass Fiber Enhanced Items | Standard | Flame Retardant With Glass Fiber | Toughening | |||||
Items | Method | Unite | 800G15 | 800G20 | 800G30 | 800G40 | 800 | 800G20-V15 | 800ST |
Physical Property | |||||||||
Specific Gravity | ASTM D792 | − | 1.01 | 1.05 | 1.12 | 1.22 | 0.91 | 1.22 | 0.9 |
Water Absorption | ASTM D570 | % | 0.05 | 0.05 | 0.04 | 0.03 | 0.06 | 0.05 | 0.07 |
Molding Shrinkage | ASTM D955 | % | 0.6-1.0 | 0.6-1.0 | 0.6-0.8 | 0.3-0.7 | 1.6-1.8 | 0.5-0.7 | 1.3-2.0 |
Melt Flow Index(200℃,10kg) | ASTM 1238 | g/10min | 6.5 | 4 | 3 | 3 | 7 | 4 | 5 |
Glass Fiber Content | − | % | 15 | 20 | 30 | 40 | − | 20 | − |
Mechanical Property | |||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 65 | 78 | 90 | 32 | 55 | 20 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 5 | 5.5 | 3.6 | 3 | 300 | 5 | >300 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 95 | 120 | 145 | 52 | 70 | 25 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2400 | 3200 | 4100 | 6400 | 1240 | 3000 | 800 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 10 | 11 | 13 | 13 | 5 | 4 | 680 |
Thermal Property | |||||||||
Heat Deflection Temperature(0.45MPa) | ASTM D648 | ℃ | 145 | 145 | 155 | 157 | 124 | 148 | 118 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB |
Electrical Property | |||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||
CTI(23℃) | IEC60112 | V | |||||||
Surface Resistivity | IEC 60093 | Ω | |||||||
Volume Resistivity | ICE 60093 | Ω.cm |