Availability: | |
---|---|
Quantity: | |
ME266U-XH
Forever
ME266U-XH is a specialized injection molding compound with a 20% mineral filling of polypropylene. It offers a remarkable combination of impact strength and stiffness, resulting in a high-quality surface finish. Designed specifically for the automotive industry, ME266U-XH is ideal for manufacturing various interior components such as pillar trims, door panels, and storage compartments.
General | ||
Form Resin Pellets | ||
Filler 20 % Mineral | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 |
Melt Flow | ISO 1133 | |
2.16 kg;230 °C | 12 g/10min | |
5 kg;230 °C | 49 g/10min | |
Ball Indentation Hardness | 62.0 MPa | ISO 2039 |
Mechanical | Nominal Value | Test Method |
Tensile Strength, Yield(50 mm/min) | 28.0 MPa | ISO 527-2 |
Elongation at Yield(50 mm/min) | 5.0 % | ISO 527-2 |
Flexural Modulus | 2500 MPa | ISO 178 |
C harpy Impact Unnotched | ISO 179 1eU | |
Temperature; -20 °C | 25.6 kJ/m² | |
Temperature; 23 °C | 52 kJ/m² | |
C harpy Impact, Notched | ISO 179 1eA | |
Temperature; -20 °C | 2.5 kJ/m² | |
Temperature; 23 °C | 6 kJ/m² | |
Thermal | Nominal Value | Test Method |
Deflection Temperature | ISO 75-2 | |
Pressure; 0.46 MPa | 115 °C | |
Pressure; 1.8 MPa | 68.0 °C | |
Vicat Softening Point(1.02 kg) | 153 °C | ISO 306 |
Processing | Nominal Value |
Processing Temperature | 220 - 260 °C |
Feed Temperature | 40.0 - 80.0 °C |
Mold Temperature | 30.0 - 50.0 °C |
Injection Velocity | 100 - 200 mm/sec |
Hold Pressure | 30.0 - 60.0 MPa |
ME266U-XH is a specialized injection molding compound with a 20% mineral filling of polypropylene. It offers a remarkable combination of impact strength and stiffness, resulting in a high-quality surface finish. Designed specifically for the automotive industry, ME266U-XH is ideal for manufacturing various interior components such as pillar trims, door panels, and storage compartments.
General | ||
Form Resin Pellets | ||
Filler 20 % Mineral | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 |
Melt Flow | ISO 1133 | |
2.16 kg;230 °C | 12 g/10min | |
5 kg;230 °C | 49 g/10min | |
Ball Indentation Hardness | 62.0 MPa | ISO 2039 |
Mechanical | Nominal Value | Test Method |
Tensile Strength, Yield(50 mm/min) | 28.0 MPa | ISO 527-2 |
Elongation at Yield(50 mm/min) | 5.0 % | ISO 527-2 |
Flexural Modulus | 2500 MPa | ISO 178 |
C harpy Impact Unnotched | ISO 179 1eU | |
Temperature; -20 °C | 25.6 kJ/m² | |
Temperature; 23 °C | 52 kJ/m² | |
C harpy Impact, Notched | ISO 179 1eA | |
Temperature; -20 °C | 2.5 kJ/m² | |
Temperature; 23 °C | 6 kJ/m² | |
Thermal | Nominal Value | Test Method |
Deflection Temperature | ISO 75-2 | |
Pressure; 0.46 MPa | 115 °C | |
Pressure; 1.8 MPa | 68.0 °C | |
Vicat Softening Point(1.02 kg) | 153 °C | ISO 306 |
Processing | Nominal Value |
Processing Temperature | 220 - 260 °C |
Feed Temperature | 40.0 - 80.0 °C |
Mold Temperature | 30.0 - 50.0 °C |
Injection Velocity | 100 - 200 mm/sec |
Hold Pressure | 30.0 - 60.0 MPa |