8202C-XH
Forever
8202C-XH is a specially designed PA6 injection molding material with a modified crystalline structure and low viscosity. It offers increased strength, stiffness, heat resistance, and performance under load, making it ideal for various applications. This material is available in heat stabilized and pigmented versions to suit different needs. Additionally, 8202C-XH has enhanced cycling capabilities while maintaining its properties and chemical resistance. It is commonly used in applications such as furniture casters, gears, window hardware, fittings, electrical insulators, bushings, valves, relays, wiring devices, and other electrical components.
General | |||
Form | Resin Pellets | ||
Feature | Medium-Low Viscosity Crystalline | Homopolymer Chemical Resistant | Excellent Processability Ec 1907/2006 (Reach) |
Bushings Fittings Furniture | |||
Usage Electrical Engineering Gear Wheels Electrical | |||
Valves/Valve Parts | |||
Physical Nominal Value Test Method | |||
Density, dry 1.13 g/cm³ ASTM D792;ISO 1183 | |||
Dry: Molding Shrinkage - Flow(3.18 mm) 0.90 % No Standard | |||
Dry: Water Absorption | |||
24 hr 1.6 % ASTM D570 | |||
24 hr;23 °C 1.6 % ISO 62 | |||
Dry: Water Absorption, Saturation | |||
9.3 % ASTM D570 | |||
23 °C 9.3 % ISO 62 | |||
Dry: Water Absorption, Equilibrium | |||
50% RH 2.6 % ASTM D570 | |||
50% RH;23 °C 2.6 % ISO 62 | |||
Dry: Rockwell Hardness, R-Scale 120 ASTM D785 | |||
Mechanical Nominal Value Test Method | |||
Dry: Tensile Modulus ISO 527-2 | |||
-40 °C 4090 MPa | |||
23 °C 3700 MPa | |||
80 °C 750 MPa | |||
120 °C 550 MPa | |||
150 °C 445 MPa |
Condition: Tensile Modulus(23 °C) | 1360 MPa | ISO 527-2 |
Dry: Tensile Strength, Yield -40 °C
80 °C
23 °C 121 °C 23 °C 120 °C 150 °C |
137 MPa
40.0 MPa
90.0 MPa 30.0 MPa 88.0 MPa 30.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 ISO 527-2 |
Condition: Tensile Strength, Yield -40 °C
80 °C
23 °C 121 °C 23 °C 120 °C |
142 MPa
30.0 MPa
48.0 MPa 25.0 MPa 43.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 |
Dry: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
130 MPa 90.0 MPa 35.0 MPa 25.0 MPa | ASTM D638 |
Condition: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
80.0 MPa 70.0 MPa 30.0 MPa 20.0 MPa | ASTM D638 |
Dry: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 27 % 4.0 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
Condition: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 30 % 22 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
Dry: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
5.0 % 12 % > 100 % > 100 % | ASTM D638 |
Condition: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
3.0 % > 100 % > 100 % > 100 % | ASTM D638 |
Dry: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
5.0 % 7.0 % > 100 % > 100 % | ISO 527-2 |
Condition: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
3.0 % > 50 % > 100 % > 100 % | ISO 527-2 |
Dry: Flexural Modulus -40 °C 23 °C 65 °C 90 °C 121 °C 23 °C |
3370 MPa 3170 MPa 600 MPa 440 MPa 385 MPa 2800 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
Condition: Flexural Modulus -40 °C 23 °C |
4200 MPa 970 MPa | ASTM D790 |
Dry: Flexural Strength -40 °C 23 °C 65 °C 121 °C 23 °C |
183 MPa 110 MPa 30.0 MPa 21.0 MPa 95.0 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
Condition: Flexural Strength -40 °C 23 °C |
168 MPa 42.0 MPa | ASTM D790 |
Dry: Charpy Notched Impact Strength(23 °C) | 3.5 kJ/m² | ISO 179 |
Dry: Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 |
Dry: Notched Izod Impact -40 °C 23 °C |
32 J/m 48 J/m | ASTM D256 |
Izod Notched Impact: condition -40 °C 23 °C |
21 J/m 170 J/m | ASTM D256 |
Dry: Drop Weight Impact Strength(23 °C) | 122 J | Internal Method |
Thermal | Nominal Value | Test Method |
Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa |
190 °C 75.0 °C 165 °C 65.0 °C |
ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A |
Dry: Peak Melting Temperature | 220 °C | ASTM D3418;ISO 3146 |
Dry: CLTE - Flow | 8.1E-5 cm/cm/°C | ASTM E831 |
Dry: RTI Elec 0.71 mm 1.5 mm 3 mm 6 mm |
125 °C 125 °C 125 °C 125 °C | UL 746 |
Dry: RTI Imp 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 75.0 °C 75.0 °C 75.0 °C | UL 746 |
Dry: RTI Str 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 85.0 °C 85.0 °C 85.0 °C | UL 746 |
Dry: Flame Rating 0.71 mm 1.5 mm 3 mm 6 mm |
V-2 V-2 V-2 V-2 | UL 94 |
Electrical | Nominal Value | Test Method |
Dry: Volume Resistivity | ||
1.5 mm | > 1.0E+15 Ohms ·cm > 1.0E+15 Ohms ·cm | ASTM D257 IEC 60093 |
Dry: Dielectric Strength, Method A, Short-Time(1.5 mm) | 30 kV/mm | ASTM D149 |
Dry: Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.15 % | |
Processing Temp, Melt<Injection> | 240 - 285 °C | |
Mold Temperature<Injection> | 65 - 80 °C | |
Injection Pressure<Injection> | 3.50 - 12.5 MPa | |
Injection Rate<Injection> | Fast |
8202C-XH is a specially designed PA6 injection molding material with a modified crystalline structure and low viscosity. It offers increased strength, stiffness, heat resistance, and performance under load, making it ideal for various applications. This material is available in heat stabilized and pigmented versions to suit different needs. Additionally, 8202C-XH has enhanced cycling capabilities while maintaining its properties and chemical resistance. It is commonly used in applications such as furniture casters, gears, window hardware, fittings, electrical insulators, bushings, valves, relays, wiring devices, and other electrical components.
General | |||
Form | Resin Pellets | ||
Feature | Medium-Low Viscosity Crystalline | Homopolymer Chemical Resistant | Excellent Processability Ec 1907/2006 (Reach) |
Bushings Fittings Furniture | |||
Usage Electrical Engineering Gear Wheels Electrical | |||
Valves/Valve Parts | |||
Physical Nominal Value Test Method | |||
Density, dry 1.13 g/cm³ ASTM D792;ISO 1183 | |||
Dry: Molding Shrinkage - Flow(3.18 mm) 0.90 % No Standard | |||
Dry: Water Absorption | |||
24 hr 1.6 % ASTM D570 | |||
24 hr;23 °C 1.6 % ISO 62 | |||
Dry: Water Absorption, Saturation | |||
9.3 % ASTM D570 | |||
23 °C 9.3 % ISO 62 | |||
Dry: Water Absorption, Equilibrium | |||
50% RH 2.6 % ASTM D570 | |||
50% RH;23 °C 2.6 % ISO 62 | |||
Dry: Rockwell Hardness, R-Scale 120 ASTM D785 | |||
Mechanical Nominal Value Test Method | |||
Dry: Tensile Modulus ISO 527-2 | |||
-40 °C 4090 MPa | |||
23 °C 3700 MPa | |||
80 °C 750 MPa | |||
120 °C 550 MPa | |||
150 °C 445 MPa |
Condition: Tensile Modulus(23 °C) | 1360 MPa | ISO 527-2 |
Dry: Tensile Strength, Yield -40 °C
80 °C
23 °C 121 °C 23 °C 120 °C 150 °C |
137 MPa
40.0 MPa
90.0 MPa 30.0 MPa 88.0 MPa 30.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 ISO 527-2 |
Condition: Tensile Strength, Yield -40 °C
80 °C
23 °C 121 °C 23 °C 120 °C |
142 MPa
30.0 MPa
48.0 MPa 25.0 MPa 43.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 |
Dry: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
130 MPa 90.0 MPa 35.0 MPa 25.0 MPa | ASTM D638 |
Condition: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
80.0 MPa 70.0 MPa 30.0 MPa 20.0 MPa | ASTM D638 |
Dry: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 27 % 4.0 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
Condition: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 30 % 22 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
Dry: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
5.0 % 12 % > 100 % > 100 % | ASTM D638 |
Condition: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
3.0 % > 100 % > 100 % > 100 % | ASTM D638 |
Dry: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
5.0 % 7.0 % > 100 % > 100 % | ISO 527-2 |
Condition: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
3.0 % > 50 % > 100 % > 100 % | ISO 527-2 |
Dry: Flexural Modulus -40 °C 23 °C 65 °C 90 °C 121 °C 23 °C |
3370 MPa 3170 MPa 600 MPa 440 MPa 385 MPa 2800 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
Condition: Flexural Modulus -40 °C 23 °C |
4200 MPa 970 MPa | ASTM D790 |
Dry: Flexural Strength -40 °C 23 °C 65 °C 121 °C 23 °C |
183 MPa 110 MPa 30.0 MPa 21.0 MPa 95.0 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
Condition: Flexural Strength -40 °C 23 °C |
168 MPa 42.0 MPa | ASTM D790 |
Dry: Charpy Notched Impact Strength(23 °C) | 3.5 kJ/m² | ISO 179 |
Dry: Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 |
Dry: Notched Izod Impact -40 °C 23 °C |
32 J/m 48 J/m | ASTM D256 |
Izod Notched Impact: condition -40 °C 23 °C |
21 J/m 170 J/m | ASTM D256 |
Dry: Drop Weight Impact Strength(23 °C) | 122 J | Internal Method |
Thermal | Nominal Value | Test Method |
Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa |
190 °C 75.0 °C 165 °C 65.0 °C |
ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A |
Dry: Peak Melting Temperature | 220 °C | ASTM D3418;ISO 3146 |
Dry: CLTE - Flow | 8.1E-5 cm/cm/°C | ASTM E831 |
Dry: RTI Elec 0.71 mm 1.5 mm 3 mm 6 mm |
125 °C 125 °C 125 °C 125 °C | UL 746 |
Dry: RTI Imp 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 75.0 °C 75.0 °C 75.0 °C | UL 746 |
Dry: RTI Str 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 85.0 °C 85.0 °C 85.0 °C | UL 746 |
Dry: Flame Rating 0.71 mm 1.5 mm 3 mm 6 mm |
V-2 V-2 V-2 V-2 | UL 94 |
Electrical | Nominal Value | Test Method |
Dry: Volume Resistivity | ||
1.5 mm | > 1.0E+15 Ohms ·cm > 1.0E+15 Ohms ·cm | ASTM D257 IEC 60093 |
Dry: Dielectric Strength, Method A, Short-Time(1.5 mm) | 30 kV/mm | ASTM D149 |
Dry: Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.15 % | |
Processing Temp, Melt<Injection> | 240 - 285 °C | |
Mold Temperature<Injection> | 65 - 80 °C | |
Injection Pressure<Injection> | 3.50 - 12.5 MPa | |
Injection Rate<Injection> | Fast |