Availability: | |
---|---|
Quantity: | |
C7230P-XH
Forever
The CYCOLOY C7230P-XH resin is a type of plastic made from a combination of polycarbonate (PC) and acrylonitrile butadiene styrene (ABS), and it contains minerals that enhance its properties. This resin is designed to be flame retardant. It offers a good combination of rigidity, smooth flow, and resistance to impact, which makes it suitable for a wide range of uses.
General | ||||
Form | Resin Pellets | |||
Filler | Mineral | |||
Feature | Enhanced Stiffness | |||
Usage Electronic Displays NoteBook Computer | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.30 g/cm³ | |||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 13 g/10min | ASTM D1238 | ||
Melt Volume-Flow Rate, MVR(260 °C;2.16 kg) | 9.00 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.25 - 0.35 % | Internal Method | ||
Water Absorption, Saturation(23 °C) | 0.090 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.040 % | ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 5200 MPa 5580 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
50 mm/min;Type I | 58.0 MPa 55.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Strength, Break | ||
50 mm/min;Type I | 45.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield | ||
50 mm/min;Type I | 4.0 % 3.8 % | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min;Type I | 32 % 30 % | ASTM D638 ISO 527-2/50 |
Flexural Modulus | ||
1.3 mm/min;50 mm;Span | 4530 MPa | ASTM D790 |
2 mm/min | 4580 MPa | ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 99.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 98.0 MPa | ASTM D790 |
C harpy Notched Impact Strength(23 °C;80*10*4;sp =62mm 0) | 5.0 kJ/m² | ISO 179 1eA |
Notched Izod Impact | ||
-30 °C | 55 J/m | ASTM D256 |
23 °C | 69 J/m | ASTM D256 |
80*10*4 mm;-30 °C | 5.0 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 5.0 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 0.00 J | ASTM D3763 |
C7230P
PC/ABS
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
1.8 MPa;3.2 mm | 88.0 °C | ASTM D648 |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 89.0 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 108 °C 107 °C 110 °C | ASTM D1525 ISO 306/B50 ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) | 4.2E-5 cm/cm/°C | |
CLTE, Transverse | ||
-40 - 40 °C | 4.9E-5 cm/cm/°C | ASTM E831 |
-40 °C | 5.9E-5 cm/cm/°C | ISO 11359-2 |
Flame Rating 1.2 mm 2 mm | V-0 5VB | UL 94 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.040 % | |
Suggested Shot Size<Injection> | 30 - 80 % | |
Rear Temperature<Injection> | 220 - 255 °C | |
Middle Temperature<injection> | 220 - 265 °C | |
Front Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Processing Temp, Melt<Injection> | 245 - 275 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.038 - 0.076 mm |
The CYCOLOY C7230P-XH resin is a type of plastic made from a combination of polycarbonate (PC) and acrylonitrile butadiene styrene (ABS), and it contains minerals that enhance its properties. This resin is designed to be flame retardant. It offers a good combination of rigidity, smooth flow, and resistance to impact, which makes it suitable for a wide range of uses.
General | ||||
Form | Resin Pellets | |||
Filler | Mineral | |||
Feature | Enhanced Stiffness | |||
Usage Electronic Displays NoteBook Computer | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.30 g/cm³ | |||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 13 g/10min | ASTM D1238 | ||
Melt Volume-Flow Rate, MVR(260 °C;2.16 kg) | 9.00 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.25 - 0.35 % | Internal Method | ||
Water Absorption, Saturation(23 °C) | 0.090 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.040 % | ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 5200 MPa 5580 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
50 mm/min;Type I | 58.0 MPa 55.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Strength, Break | ||
50 mm/min;Type I | 45.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield | ||
50 mm/min;Type I | 4.0 % 3.8 % | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min;Type I | 32 % 30 % | ASTM D638 ISO 527-2/50 |
Flexural Modulus | ||
1.3 mm/min;50 mm;Span | 4530 MPa | ASTM D790 |
2 mm/min | 4580 MPa | ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 99.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 98.0 MPa | ASTM D790 |
C harpy Notched Impact Strength(23 °C;80*10*4;sp =62mm 0) | 5.0 kJ/m² | ISO 179 1eA |
Notched Izod Impact | ||
-30 °C | 55 J/m | ASTM D256 |
23 °C | 69 J/m | ASTM D256 |
80*10*4 mm;-30 °C | 5.0 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 5.0 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 0.00 J | ASTM D3763 |
C7230P
PC/ABS
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
1.8 MPa;3.2 mm | 88.0 °C | ASTM D648 |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 89.0 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 108 °C 107 °C 110 °C | ASTM D1525 ISO 306/B50 ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) | 4.2E-5 cm/cm/°C | |
CLTE, Transverse | ||
-40 - 40 °C | 4.9E-5 cm/cm/°C | ASTM E831 |
-40 °C | 5.9E-5 cm/cm/°C | ISO 11359-2 |
Flame Rating 1.2 mm 2 mm | V-0 5VB | UL 94 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.040 % | |
Suggested Shot Size<Injection> | 30 - 80 % | |
Rear Temperature<Injection> | 220 - 255 °C | |
Middle Temperature<injection> | 220 - 265 °C | |
Front Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Processing Temp, Melt<Injection> | 245 - 275 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.038 - 0.076 mm |