W1000JiQ-XH
Forever
The W1000JiQ-XH compound is a plastic material that is primarily made from Polybutylene terephthalate (PBT) resin. This PBT resin is produced using ELCRIN iQ upcycling technology, which incorporates at least 56% of recycled materials from post-consumer sources. The compound offers various beneficial attributes such as biocompatibility according to the ISO10993 standard, improved processing capabilities, low extractables, and suitability for healthcare applications. It can be used in a wide range of products including sprinklers, nozzles, pumps, and cosmetic packages.
General | |||
Form | Resin Pellets | ||
Feature | Biocompatible Fda Low Extractables Pcr | 56 % Pcr | |
Usage | Consumer Healthcare Building and Construction | Packaging | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity |
1.31 1.31 g/cm³ |
ASTM D792 ISO 1183 | |
Melt Flow Rate[MFR](250 °C;2.16 kgf) | 23 g/10min | ASTM D1238 | |
Water Absorption(23 °C;saturated) | 0.16 % | ISO 62-1 | |
Moisture Absorption(50% RH;23 °C) | 0.07 % | ISO 62 | |
Melt Volume Rate, MVR(2.16 kg;MVR at 250 °C) | 21 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 50 J/m | ASTM D256 |
-30 °C | 46 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 2 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 61 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 5 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 56 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 29 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 3.2 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 140 % | ASTM D638 |
50 mm/min | 130 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2550 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 84 MPa | ASTM D790 |
2 mm/min | 80 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2560 MPa | ASTM D790 |
2 mm/min | 2430 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 48 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.8E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.8E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 8.1e-05 1/°C | ASTM E831 |
-40 - 40 °C | 8.1e-05 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 133 °C | ISO 75/Bf |
Vicat Softening Temperature(Rate B/120) | 168 °C | ISO 306 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 12 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 245 - 260 °C | |
Nozzle Temperature<Injection> | 240 - 255 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 260 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 250 °C | |
Mold Temperature<Injection> | 50 - 75 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 50 - 100 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.013 - 0.025 mm |
The W1000JiQ-XH compound is a plastic material that is primarily made from Polybutylene terephthalate (PBT) resin. This PBT resin is produced using ELCRIN iQ upcycling technology, which incorporates at least 56% of recycled materials from post-consumer sources. The compound offers various beneficial attributes such as biocompatibility according to the ISO10993 standard, improved processing capabilities, low extractables, and suitability for healthcare applications. It can be used in a wide range of products including sprinklers, nozzles, pumps, and cosmetic packages.
General | |||
Form | Resin Pellets | ||
Feature | Biocompatible Fda Low Extractables Pcr | 56 % Pcr | |
Usage | Consumer Healthcare Building and Construction | Packaging | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity |
1.31 1.31 g/cm³ |
ASTM D792 ISO 1183 | |
Melt Flow Rate[MFR](250 °C;2.16 kgf) | 23 g/10min | ASTM D1238 | |
Water Absorption(23 °C;saturated) | 0.16 % | ISO 62-1 | |
Moisture Absorption(50% RH;23 °C) | 0.07 % | ISO 62 | |
Melt Volume Rate, MVR(2.16 kg;MVR at 250 °C) | 21 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 50 J/m | ASTM D256 |
-30 °C | 46 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 2 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 61 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 5 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 56 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 29 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 3.2 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 140 % | ASTM D638 |
50 mm/min | 130 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2550 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 84 MPa | ASTM D790 |
2 mm/min | 80 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2560 MPa | ASTM D790 |
2 mm/min | 2430 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 48 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.8E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.8E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 8.1e-05 1/°C | ASTM E831 |
-40 - 40 °C | 8.1e-05 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 133 °C | ISO 75/Bf |
Vicat Softening Temperature(Rate B/120) | 168 °C | ISO 306 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 12 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 245 - 260 °C | |
Nozzle Temperature<Injection> | 240 - 255 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 260 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 250 °C | |
Mold Temperature<Injection> | 50 - 75 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 50 - 100 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.013 - 0.025 mm |