BM5225Y-XH
Forever
BM5225Y-XH Polycarbonate resin is a type of flame retardant grade that is suitable for injection molding. It is non chlorinated/brominated and contains mineral fillers to enhance its flame resistance. This resin offers high modulus, good flow, ductility, and low warpage during the molding process. It has achieved a UL94 V0@1.5mm and 5VB@1.5mm flame rating, making it ideal for applications requiring flame resistance. Additionally, its properties make it well-suited for thin wall applications.
General | ||||
Form | Resin Pellets | |||
Feature | Low Warpage | Non-Brominated & Non-Chlorinated Flame Retardant Non-Chlorinated | ||
Usage | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.39 1.4 g/cm³ |
ASTM D792 ISO 1183 | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 12 g/10min | ASTM D1238 | ||
Hardness, Rockwell R | 109 | ASTM D785 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched 23 °C -30 °C |
50 J/m 37 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 20 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 6 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
5 mm/min;Type I | 55 MPa | ASTM D638 |
5 mm/min | 56 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 34 MPa | ASTM D638 |
5 mm/min | 30 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 2.8 % | ASTM D638 |
5 mm/min | 2.8 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 5 % | ASTM D638 |
5 mm/min | 5 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 5850 MPa | ASTM D638 |
1 mm/min | 5570 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 98 MPa | ASTM D790 |
2 mm/min | 98 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 6010 MPa | ASTM D790 |
2 mm/min | 6150 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 1.2 mm ≥ 0.8 mm |
5VB V-0 V-1 | UL 94 |
Vicat Softening Temperature(Rate B/50) | 98 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
93 °C 85 °C | ASTM D648 |
CTE, Flow(23°C to 80°C) | 3.4e-05 1/°C | ISO 11359-2 |
CTE, XFlow(23°C to 80°C) | 6.9e-05 1/°C | ISO 11359-2 |
HDT/Af(1.8) | 87 °C | ISO 75/Af |
Relative Temp Index, Elec | 80 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 90 - 105 °C | |
Drying Time<Injection> | 4 - 6 hrs | |
Drying Time, Cumulative<Injection> | 16 hrs | |
Melt Temperature<Injection> | 270 - 300 °C | |
Nozzle Temperature<Injection> | 280 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 260 - 280 °C | |
Rear, Zone 1 Temperature<Injection> | 250 - 270 °C | |
Mold Temperature<Injection> | 70 - 90 °C |
BM5225Y-XH Polycarbonate resin is a type of flame retardant grade that is suitable for injection molding. It is non chlorinated/brominated and contains mineral fillers to enhance its flame resistance. This resin offers high modulus, good flow, ductility, and low warpage during the molding process. It has achieved a UL94 V0@1.5mm and 5VB@1.5mm flame rating, making it ideal for applications requiring flame resistance. Additionally, its properties make it well-suited for thin wall applications.
General | ||||
Form | Resin Pellets | |||
Feature | Low Warpage | Non-Brominated & Non-Chlorinated Flame Retardant Non-Chlorinated | ||
Usage | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.39 1.4 g/cm³ |
ASTM D792 ISO 1183 | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 12 g/10min | ASTM D1238 | ||
Hardness, Rockwell R | 109 | ASTM D785 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched 23 °C -30 °C |
50 J/m 37 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 20 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 6 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
5 mm/min;Type I | 55 MPa | ASTM D638 |
5 mm/min | 56 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 34 MPa | ASTM D638 |
5 mm/min | 30 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 2.8 % | ASTM D638 |
5 mm/min | 2.8 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 5 % | ASTM D638 |
5 mm/min | 5 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 5850 MPa | ASTM D638 |
1 mm/min | 5570 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 98 MPa | ASTM D790 |
2 mm/min | 98 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 6010 MPa | ASTM D790 |
2 mm/min | 6150 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 1.2 mm ≥ 0.8 mm |
5VB V-0 V-1 | UL 94 |
Vicat Softening Temperature(Rate B/50) | 98 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
93 °C 85 °C | ASTM D648 |
CTE, Flow(23°C to 80°C) | 3.4e-05 1/°C | ISO 11359-2 |
CTE, XFlow(23°C to 80°C) | 6.9e-05 1/°C | ISO 11359-2 |
HDT/Af(1.8) | 87 °C | ISO 75/Af |
Relative Temp Index, Elec | 80 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 90 - 105 °C | |
Drying Time<Injection> | 4 - 6 hrs | |
Drying Time, Cumulative<Injection> | 16 hrs | |
Melt Temperature<Injection> | 270 - 300 °C | |
Nozzle Temperature<Injection> | 280 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 260 - 280 °C | |
Rear, Zone 1 Temperature<Injection> | 250 - 270 °C | |
Mold Temperature<Injection> | 70 - 90 °C |