3-8097 VP-XH
Forever
Product Description | |||
3-8097 VP-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts. | |||
General | |||
Form | |||
Feature | Thermally
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.56 g/cm³ | ISO 1183 | |
Linear Mold Shrinkage | 0.2 - 0.5 % | ||
Mechanical | Nominal Value | Test Method | |
Tensile Strength | 140 MPa | ||
Elongation at Break | 1.60 % | ||
Modulus of Elasticity | 1.6E+4 MPa | ||
Flexural Strength(Strain 2.1 %) | 215 MPa | ||
Flexural Modulus | 1.4E+4 MPa | ||
C harpy Impact Unnotched(23 °C) | 30 kJ/m² | ISO 179 1eU | |
Thermal | Nominal Value | Test Method | |
Thermal Conductivity, In Plane(Hot Disk;Parallel 60x60x3 3.50 W/m-K mm) | |||
Maximum Service Temperature, Air | |||
Continuous | 90.0 °C | ||
Short Term | 210 °C | ||
Deflection Temperature(Pressure; 1.8 MPa) | 200 °C | ||
Electrical | Nominal Value | Test Method | |
Volume Resistivity(10V) | > = 1.00e+6 ohms ·cm | ||
Surface Resistance(10 V) | > = 1.00e+6 Ohms |
Processing | Nominal Value |
Nozzle Temperature | 270 - 280 °C |
Zone 1 | 250 - 270 °C |
Barrel - Zone 2 Temperature | 270 - 290 °C |
Barrel - Zone 3 Temperature | 280 - 300 °C |
Melt Temperature | 270 °C |
Mold Temperature | 70.0 - 110 °C |
Drying Temperature | |
Time 10 - 16 hr | 75.0 °C |
Time 4 - 6 hr | 105 °C |
Product Description | |||
3-8097 VP-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts. | |||
General | |||
Form | |||
Feature | Thermally
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.56 g/cm³ | ISO 1183 | |
Linear Mold Shrinkage | 0.2 - 0.5 % | ||
Mechanical | Nominal Value | Test Method | |
Tensile Strength | 140 MPa | ||
Elongation at Break | 1.60 % | ||
Modulus of Elasticity | 1.6E+4 MPa | ||
Flexural Strength(Strain 2.1 %) | 215 MPa | ||
Flexural Modulus | 1.4E+4 MPa | ||
C harpy Impact Unnotched(23 °C) | 30 kJ/m² | ISO 179 1eU | |
Thermal | Nominal Value | Test Method | |
Thermal Conductivity, In Plane(Hot Disk;Parallel 60x60x3 3.50 W/m-K mm) | |||
Maximum Service Temperature, Air | |||
Continuous | 90.0 °C | ||
Short Term | 210 °C | ||
Deflection Temperature(Pressure; 1.8 MPa) | 200 °C | ||
Electrical | Nominal Value | Test Method | |
Volume Resistivity(10V) | > = 1.00e+6 ohms ·cm | ||
Surface Resistance(10 V) | > = 1.00e+6 Ohms |
Processing | Nominal Value |
Nozzle Temperature | 270 - 280 °C |
Zone 1 | 250 - 270 °C |
Barrel - Zone 2 Temperature | 270 - 290 °C |
Barrel - Zone 3 Temperature | 280 - 300 °C |
Melt Temperature | 270 °C |
Mold Temperature | 70.0 - 110 °C |
Drying Temperature | |
Time 10 - 16 hr | 75.0 °C |
Time 4 - 6 hr | 105 °C |