Availability: | |
---|---|
Quantity: | |
LUX9136-XH-2
FOREVER
Product Description | ||||
Introducing LUX9136C-XH Polycarbonate (PC) resin - a premium, non-filled grade designed specifically for injection molding applications. Engineered with outstanding performance in mind, this flame retardant PC is formulated without chlorinated or brominated compounds, making it a safer and more environmentally friendly choice for your project. With its impressive UL-94 V0 rating at 1.5 mm thickness, rest assured that this resin offers exceptional fire resistance properties. But that's not all - LUX9136C-XH showcases remarkable high flow capability, allowing for seamless filling of intricate molds and ensuring smooth and precise part production. Moreover, its UV stabilization feature adds an extra layer of protection against weathering, making it suitable for applications exposed to various outdoor conditions. Available in a range of diffusion colors, LUX9136C-XH offers versatility and aesthetic appeal, letting you create visually stunning end products that stand out from the crowd. Choose LUX9136C-XH Polycarbonate (PC) resin for uncompromising performance, safety, and design possibilities. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | F1 | Excellent Processability Diffusive | Non-Brominated & Non- Chlorinated Flame Retardant | |
Uses Lighting Diffusers | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.19 1.2 g/cm³ | ASTM D792 ISO 1183 | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.13 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | f1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched 23 °C -30 °C | NB J/m NB J/m | ASTM D4812 | ||
Izod Impact, Notched 23 °C -30 °C | 100 J/m 85 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | ||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 10 kJ/m² 9 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | 10 kJ/m² 9 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield | ||
50 mm/min;Type I | 67 MPa | ASTM D638 |
50 mm/min | 63 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 54 MPa | ASTM D638 |
50 mm/min | 57 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 6 % | ASTM D638 |
50 mm/min | 6 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 80 % | ASTM D638 |
50 mm/min | 73 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2400 MPa | ASTM D638 |
1 mm/min | 2300 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 103 MPa | ASTM D790 |
2 mm/min | 96 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 |
2 mm/min | 2400 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 0.4 mm | V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm | 850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm | 960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 136 °C 139 °C 140 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 130 °C 120 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C | 6.8E-05 1/°C 7.7e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C | 7.0E-05 1/°C 8.0e-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 121 °C | ISO 75/Ae |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.78 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.6E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.4 mm | PLC 0 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.4 mm) | PLC 1 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth <Injection> | 0.025 - 0.076 mm |
Product Description | ||||
Introducing LUX9136C-XH Polycarbonate (PC) resin - a premium, non-filled grade designed specifically for injection molding applications. Engineered with outstanding performance in mind, this flame retardant PC is formulated without chlorinated or brominated compounds, making it a safer and more environmentally friendly choice for your project. With its impressive UL-94 V0 rating at 1.5 mm thickness, rest assured that this resin offers exceptional fire resistance properties. But that's not all - LUX9136C-XH showcases remarkable high flow capability, allowing for seamless filling of intricate molds and ensuring smooth and precise part production. Moreover, its UV stabilization feature adds an extra layer of protection against weathering, making it suitable for applications exposed to various outdoor conditions. Available in a range of diffusion colors, LUX9136C-XH offers versatility and aesthetic appeal, letting you create visually stunning end products that stand out from the crowd. Choose LUX9136C-XH Polycarbonate (PC) resin for uncompromising performance, safety, and design possibilities. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | F1 | Excellent Processability Diffusive | Non-Brominated & Non- Chlorinated Flame Retardant | |
Uses Lighting Diffusers | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.19 1.2 g/cm³ | ASTM D792 ISO 1183 | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.13 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | f1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched 23 °C -30 °C | NB J/m NB J/m | ASTM D4812 | ||
Izod Impact, Notched 23 °C -30 °C | 100 J/m 85 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | ||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 10 kJ/m² 9 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | 10 kJ/m² 9 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield | ||
50 mm/min;Type I | 67 MPa | ASTM D638 |
50 mm/min | 63 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 54 MPa | ASTM D638 |
50 mm/min | 57 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 6 % | ASTM D638 |
50 mm/min | 6 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 80 % | ASTM D638 |
50 mm/min | 73 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2400 MPa | ASTM D638 |
1 mm/min | 2300 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 103 MPa | ASTM D790 |
2 mm/min | 96 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 |
2 mm/min | 2400 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 0.4 mm | V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm | 850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm | 960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 136 °C 139 °C 140 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 130 °C 120 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C | 6.8E-05 1/°C 7.7e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C | 7.0E-05 1/°C 8.0e-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 121 °C | ISO 75/Ae |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.78 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.6E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.4 mm | PLC 0 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.4 mm) | PLC 1 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth <Injection> | 0.025 - 0.076 mm |