HMG47MD-XH
Forever
Universal injection molded ABS for household appliances, electronic displays, fluid processing, and medical applications. Biocompatibility (ISO 10993).Biocompatible (ISO 10993). FDA compliant. Gamma & EtO sterilizable.
General | ||||||
Form | Resin Pellets | |||||
Feature | Biocompatible Fda | Medical Disinfection Application
X-Ray Sterilizable | Gamma Sterilizable Eto Sterilization | |||
|
|
| ||||
Usage | Lawn And Garden Equipment Appliances | Pharmaceuticals Electronic Displays | Outdoor Fluid Handling | |||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.05 g/cm³ | |||||
Melt Mass-Flow Rate, MFR | ||||||
230 °C;3.8 kg | 5.6 g/10min | ASTM D1238 | ||||
220 °C;10 kg | 19 g/10min | ISO 1133 | ||||
Molding Shrinkage, Flow(3.2 | mm) | 0.50 - 0.80 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2270 MPa 2530 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
5 mm/min;Type I | 44.0 MPa 50.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Strength, Break | ||
5 mm/min;Type I | 33.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Yield | ||
5 mm/min;Type I | 2.0 % 2.6 % | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Break | ||
5 mm/min;Type I | 24 % 25 % | ASTM D638 ISO 527-2/5 |
Flexural Modulus | ||
1.3 mm/min;50 mm;Span | 2340 MPa | ASTM D790 |
2 mm/min | 2410 MPa | ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 76.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 72.0 MPa | ASTM D790 |
Notched Izod Impact | ||
-30 °C | 130 J/m | ASTM D256 |
23 °C | 320 J/m | ASTM D256 |
80*10*4 mm;-30 °C | 8.0 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 23 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 30.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa;3.2 mm | 94.0 °C | ASTM D648 |
1.8 MPa;3.2 mm | 80.0 °C | ASTM D648 |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 80.0 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 98.0 °C 100 °C | ASTM D1525 ISO 306/B50 |
CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse(-40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 95 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.10 % | |
Suggested Shot Size<Injection> | 50 - 70 % | |
Rear Temperature<Injection> | 190 - 210 °C | |
Middle Temperature<injection> | 205 - 225 °C | |
Front Temperature<Injection> | 215 - 240 °C | |
Nozzle Temperature<Injection> | 220 - 260 °C | |
Processing Temp, Melt<Injection> | 220 - 260 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 30 - 60 rpm | |
Vent Depth <Injection> | 0.038 - 0.051 mm |
Universal injection molded ABS for household appliances, electronic displays, fluid processing, and medical applications. Biocompatibility (ISO 10993).Biocompatible (ISO 10993). FDA compliant. Gamma & EtO sterilizable.
General | ||||||
Form | Resin Pellets | |||||
Feature | Biocompatible Fda | Medical Disinfection Application
X-Ray Sterilizable | Gamma Sterilizable Eto Sterilization | |||
|
|
| ||||
Usage | Lawn And Garden Equipment Appliances | Pharmaceuticals Electronic Displays | Outdoor Fluid Handling | |||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.05 g/cm³ | |||||
Melt Mass-Flow Rate, MFR | ||||||
230 °C;3.8 kg | 5.6 g/10min | ASTM D1238 | ||||
220 °C;10 kg | 19 g/10min | ISO 1133 | ||||
Molding Shrinkage, Flow(3.2 | mm) | 0.50 - 0.80 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2270 MPa 2530 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
5 mm/min;Type I | 44.0 MPa 50.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Strength, Break | ||
5 mm/min;Type I | 33.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Yield | ||
5 mm/min;Type I | 2.0 % 2.6 % | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Break | ||
5 mm/min;Type I | 24 % 25 % | ASTM D638 ISO 527-2/5 |
Flexural Modulus | ||
1.3 mm/min;50 mm;Span | 2340 MPa | ASTM D790 |
2 mm/min | 2410 MPa | ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 76.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 72.0 MPa | ASTM D790 |
Notched Izod Impact | ||
-30 °C | 130 J/m | ASTM D256 |
23 °C | 320 J/m | ASTM D256 |
80*10*4 mm;-30 °C | 8.0 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 23 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 30.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa;3.2 mm | 94.0 °C | ASTM D648 |
1.8 MPa;3.2 mm | 80.0 °C | ASTM D648 |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 80.0 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 98.0 °C 100 °C | ASTM D1525 ISO 306/B50 |
CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse(-40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 95 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.10 % | |
Suggested Shot Size<Injection> | 50 - 70 % | |
Rear Temperature<Injection> | 190 - 210 °C | |
Middle Temperature<injection> | 205 - 225 °C | |
Front Temperature<Injection> | 215 - 240 °C | |
Nozzle Temperature<Injection> | 220 - 260 °C | |
Processing Temp, Melt<Injection> | 220 - 260 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 30 - 60 rpm | |
Vent Depth <Injection> | 0.038 - 0.051 mm |