Flame-retardant PP plastics are widely used in electronic appliances, home appliances, automobiles and other industries. Widely used in power supply, heater shell switch, electric kettle base, terminal block, home appliance shell, microwave oven shell, induction cooker shell, motor base, washing machine parts, electric iron parts, electric oven parts.
Technical Data Sheet | Glass Fiber Enhanced Items | Standard | Flame Retardant With Glass Fiber | Toughening | |||||
Items | Method | Unite | 800G15 | 800G20 | 800G30 | 800G40 | 800 | 800G20-V15 | 800ST |
Physical Property | |||||||||
Specific Gravity | ASTM D792 | − | 1.01 | 1.05 | 1.12 | 1.22 | 0.91 | 1.22 | 0.9 |
Water Absorption | ASTM D570 | % | 0.05 | 0.05 | 0.04 | 0.03 | 0.06 | 0.05 | 0.07 |
Molding Shrinkage | ASTM D955 | % | 0.6-1.0 | 0.6-1.0 | 0.6-0.8 | 0.3-0.7 | 1.6-1.8 | 0.5-0.7 | 1.3-2.0 |
Melt Flow Index(200℃,10kg) | ASTM 1238 | g/10min | 6.5 | 4 | 3 | 3 | 7 | 4 | 5 |
Glass Fiber Content | − | % | 15 | 20 | 30 | 40 | − | 20 | − |
Mechanical Property | |||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 65 | 78 | 90 | 32 | 55 | 20 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 5 | 5.5 | 3.6 | 3 | 300 | 5 | >300 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 95 | 120 | 145 | 52 | 70 | 25 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2400 | 3200 | 4100 | 6400 | 1240 | 3000 | 800 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 10 | 11 | 13 | 13 | 5 | 4 | 680 |
Thermal Property | |||||||||
Heat Deflection Temperature(0.45MPa) | ASTM D648 | ℃ | 145 | 145 | 155 | 157 | 124 | 148 | 118 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB |
Electrical Property | |||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||
CTI(23℃) | IEC60112 | V | |||||||
Surface Resistivity | IEC 60093 | Ω | |||||||
Volume Resistivity | ICE 60093 | Ω.cm |
Flame-retardant PP plastics are widely used in electronic appliances, home appliances, automobiles and other industries. Widely used in power supply, heater shell switch, electric kettle base, terminal block, home appliance shell, microwave oven shell, induction cooker shell, motor base, washing machine parts, electric iron parts, electric oven parts.
Technical Data Sheet | Glass Fiber Enhanced Items | Standard | Flame Retardant With Glass Fiber | Toughening | |||||
Items | Method | Unite | 800G15 | 800G20 | 800G30 | 800G40 | 800 | 800G20-V15 | 800ST |
Physical Property | |||||||||
Specific Gravity | ASTM D792 | − | 1.01 | 1.05 | 1.12 | 1.22 | 0.91 | 1.22 | 0.9 |
Water Absorption | ASTM D570 | % | 0.05 | 0.05 | 0.04 | 0.03 | 0.06 | 0.05 | 0.07 |
Molding Shrinkage | ASTM D955 | % | 0.6-1.0 | 0.6-1.0 | 0.6-0.8 | 0.3-0.7 | 1.6-1.8 | 0.5-0.7 | 1.3-2.0 |
Melt Flow Index(200℃,10kg) | ASTM 1238 | g/10min | 6.5 | 4 | 3 | 3 | 7 | 4 | 5 |
Glass Fiber Content | − | % | 15 | 20 | 30 | 40 | − | 20 | − |
Mechanical Property | |||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 65 | 78 | 90 | 32 | 55 | 20 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 5 | 5.5 | 3.6 | 3 | 300 | 5 | >300 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 95 | 120 | 145 | 52 | 70 | 25 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2400 | 3200 | 4100 | 6400 | 1240 | 3000 | 800 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 10 | 11 | 13 | 13 | 5 | 4 | 680 |
Thermal Property | |||||||||
Heat Deflection Temperature(0.45MPa) | ASTM D648 | ℃ | 145 | 145 | 155 | 157 | 124 | 148 | 118 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB |
Electrical Property | |||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||
CTI(23℃) | IEC60112 | V | |||||||
Surface Resistivity | IEC 60093 | Ω | |||||||
Volume Resistivity | ICE 60093 | Ω.cm |