Our PC modified materials mainly include flame-retardant PC, reinforced PC, high-flow flame-retardant PC, toughened PC, and light-diffusing PC. The material has the characteristics of light weight, high transparency, good impact resistance, good dimensional stability, weather resistance, good electrical insulation properties, and easy processing and molding. Modified PC materials are widely used in Auto parts, lighting, OA products, electronic appliances and other fields.
Technical Data Sheet | General Grade | Glass Fiber Enhanced | Flame Retardant | Flame Retardant With Glass Fiber | Light Diffusion | ||||||||||||||
Items | Method | Unite | 100 | 100-15 | 100-20 | 100-50 | 100G10 | 100G20 | 100G30 | 100G40 | 100-10V30 | 100-10V15 | 100-20V30 | 100-20V15 | 100G05-V15 | 100G10-V15 | 100G20-V15 | 100G30-V15 | 100-1218 |
Physical Property | |||||||||||||||||||
Specific Gravity | ASTM D792 | − | 1.2 | 1.2 | 1.2 | 1.2 | 1.25 | 1.32 | 1.42 | 1.5 | 1.2 | 1.2 | 1.2 | 1.2 | 1.22 | 1.24 | 1.34 | 1.42 | 1.2 |
Water Absorption | ASTM D570 | % | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.19 | 0.18 | 0.17 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.19 | 0.2 | 0.2 |
Molding Shrinkage | ASTM D955 | % | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.3-0.5 | 0.2-.04 | 0.1-0.3 | 0.1-0.2 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.4-0.6 | 0.3-0.5 | 0.2-0.4 | 0.1-0.3 | 0.5-0.7 |
Melt Flow Index(300℃,1.2kg) | ASTM D1238 | g/10min | 10 | 15 | 20 | 50 | 12 | 11 | 10 | 8 | 10 | 10 | 20 | 20 | 15 | 10 | 10 | 8 | 10 |
Mechanical Property | |||||||||||||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 60 | 63 | 55 | 80 | 110 | 120 | 140 | 60 | 60 | 60 | 63 | 65 | 60 | 100 | 120 | 63 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | ≥80 | ≥80 | ≥70 | ≥40 | 8 | 6 | 3 | 3 | ≥70 | ≥70 | ≥70 | ≥70 | ≥10 | ≥80 | ≥5 | ≥3 | ≥80 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 90 | 90 | 95 | 100 | 130 | 150 | 180 | 90 | 90 | 90 | 90 | 120 | 95 | 130 | 150 | 90 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2300 | 2300 | 2300 | 2200 | 3300 | 4600 | 6000 | 8000 | 2300 | 2300 | 2300 | 2300 | 2400 | 2300 | 5000 | 6800 | 2300 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 80 | 75 | 75 | 50 | 9 | 9 | 10 | 8 | 75 | 70 | 75 | 70 | 20 | 65 | 10 | 12 | 75 |
Thermal Property | |||||||||||||||||||
Heat Deflection Temperature(1.8MPa) | ASTM D648 | ℃ | 130 | 130 | 128 | 125 | 130 | 134 | 140 | 140 | 140 | 130 | 128 | 128 | 128 | 115 | 136 | 140 | 130 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | − | − | − | − | V0 | − | V0 | V0 | V0 | V0 | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | V2 | V2 | V2 | V2 | V0 | V0 | V0 | V0 | V0 | V0 | V0 | V0 | V2 |
Electrical Property | |||||||||||||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | |
CTI(23℃) | IEC60112 | V | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | |
Surface Resistivity | IEC 60093 | Ω | |||||||||||||||||
Volume Resistivity | ICE 60093 | Ω.cm |
Our PC modified materials mainly include flame-retardant PC, reinforced PC, high-flow flame-retardant PC, toughened PC, and light-diffusing PC. The material has the characteristics of light weight, high transparency, good impact resistance, good dimensional stability, weather resistance, good electrical insulation properties, and easy processing and molding. Modified PC materials are widely used in Auto parts, lighting, OA products, electronic appliances and other fields.
Technical Data Sheet | General Grade | Glass Fiber Enhanced | Flame Retardant | Flame Retardant With Glass Fiber | Light Diffusion | ||||||||||||||
Items | Method | Unite | 100 | 100-15 | 100-20 | 100-50 | 100G10 | 100G20 | 100G30 | 100G40 | 100-10V30 | 100-10V15 | 100-20V30 | 100-20V15 | 100G05-V15 | 100G10-V15 | 100G20-V15 | 100G30-V15 | 100-1218 |
Physical Property | |||||||||||||||||||
Specific Gravity | ASTM D792 | − | 1.2 | 1.2 | 1.2 | 1.2 | 1.25 | 1.32 | 1.42 | 1.5 | 1.2 | 1.2 | 1.2 | 1.2 | 1.22 | 1.24 | 1.34 | 1.42 | 1.2 |
Water Absorption | ASTM D570 | % | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.19 | 0.18 | 0.17 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.19 | 0.2 | 0.2 |
Molding Shrinkage | ASTM D955 | % | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.3-0.5 | 0.2-.04 | 0.1-0.3 | 0.1-0.2 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | 0.4-0.6 | 0.3-0.5 | 0.2-0.4 | 0.1-0.3 | 0.5-0.7 |
Melt Flow Index(300℃,1.2kg) | ASTM D1238 | g/10min | 10 | 15 | 20 | 50 | 12 | 11 | 10 | 8 | 10 | 10 | 20 | 20 | 15 | 10 | 10 | 8 | 10 |
Mechanical Property | |||||||||||||||||||
Tensile Strength(50mm/min) | ASTM D638 | MPa | 60 | 60 | 63 | 55 | 80 | 110 | 120 | 140 | 60 | 60 | 60 | 63 | 65 | 60 | 100 | 120 | 63 |
Elongation tensile Stretch(50mm/min) | ASTM D638 | % | ≥80 | ≥80 | ≥70 | ≥40 | 8 | 6 | 3 | 3 | ≥70 | ≥70 | ≥70 | ≥70 | ≥10 | ≥80 | ≥5 | ≥3 | ≥80 |
Flexural Strength(10mm/min) | ASTM D790 | MPa | 90 | 90 | 90 | 95 | 100 | 130 | 150 | 180 | 90 | 90 | 90 | 90 | 120 | 95 | 130 | 150 | 90 |
Flexural Modulus(10mm/min) | ASTM D790 | MPa | 2300 | 2300 | 2300 | 2200 | 3300 | 4600 | 6000 | 8000 | 2300 | 2300 | 2300 | 2300 | 2400 | 2300 | 5000 | 6800 | 2300 |
Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 80 | 75 | 75 | 50 | 9 | 9 | 10 | 8 | 75 | 70 | 75 | 70 | 20 | 65 | 10 | 12 | 75 |
Thermal Property | |||||||||||||||||||
Heat Deflection Temperature(1.8MPa) | ASTM D648 | ℃ | 130 | 130 | 128 | 125 | 130 | 134 | 140 | 140 | 140 | 130 | 128 | 128 | 128 | 115 | 136 | 140 | 130 |
Flammability | UL94 | 1.5mm | − | − | − | − | − | − | − | − | − | V0 | − | V0 | V0 | V0 | V0 | V0 | − |
Flammability | UL94 | 3.0mm | HB | HB | HB | HB | V2 | V2 | V2 | V2 | V0 | V0 | V0 | V0 | V0 | V0 | V0 | V0 | V2 |
Electrical Property | |||||||||||||||||||
Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | |
CTI(23℃) | IEC60112 | V | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | 350 | |
Surface Resistivity | IEC 60093 | Ω | |||||||||||||||||
Volume Resistivity | ICE 60093 | Ω.cm |