Availability: | |
---|---|
Quantity: | |
EXL9112-XH
FOREVER
The high-quality, opaque PC-Siloxane copolymer, designed to meet the demands of modern manufacturing processes.
With excellent processability and improved flow, this product offers the convenience of handling ease with superb performance. Its low temperature ductility allows for ease of use in a range of applications.
Furthermore, this product is non-chlorinated and non-brominated, making it an eco-friendly option for those searching for green solutions. With UL rating of V-0/5VA, you can rest assured about its fire resistance properties.
General | |||||
Form | Resin Pellets | ||||
Feature | Low Temperature Impact | Outdoor Non-Chlorinated | F1 Excellent Processability | ||
Non-Brominated Hi h Im act | |||||
Consumer Electrical | Healthcare | Industria | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.18 1.19 g/cm³ | ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 17 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 16 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion | 1 | UL 746C | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 731 J/m 560 J/m 53 kJ/m² 18 kJ/m² | ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | |||
Instrumented Dart Impact, Total Energy(23 °C) | 67 J | ASTM D3763 | |||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 55 kJ/m² 20 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 | 60 kJ/m² 25 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min | 58 MPa 59 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min | 58 MPa 55 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min | 5.8 % 5 % | ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min | 103 % 100 % | ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min | 2260 MPa 2200 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 95 MPa 88 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2330 MPa 2300 MPa | ASTM D790 ISO 178 |
Ball Indentation Hardness(H358/30) | 95 MPa | ISO 2039-1 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 2.5 mm ≥ 0.8 mm ≥ 1.5 mm | 5VA 5VB HB V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 2.5 mm 3 mm 2 mm 1.5 mm 1 mm | 825 °C 825 °C 825 °C 825 °C 825 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 2.5 mm 3 mm 2 mm 1.5 mm 1 mm | 960 °C 960 °C 960 °C 960 °C 960 °C | IEC 60695-2-12 |
Oxygen Index | 40 % | ISO 4589 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 143 °C 143 °C 144 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 136 °C 123 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C | 7.2e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C | 7.2e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp=100mm; 0.45 Mpa) | 136 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 124 °C | ISO 75/Ae |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Strength, in Oil(3.2 mm) | 19 kV/mm | IEC 60243-1 |
Relative Permittivity 1.0e+6 Hz 50/60 Hz | 2.7 2.7 | IEC 60250 |
Dissipation Factor 50/60 Hz 1.0e+6 Hz | 4.0E-04 1.0E-02 | IEC 60250 |
Comparative Tracking Index | 175 V | IEC 60112 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 0.8 mm | PLC 2 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI ≥ 1.5 mm ≥ 0.8 mm | PLC 0 PLC 3 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |
Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
The high-quality, opaque PC-Siloxane copolymer, designed to meet the demands of modern manufacturing processes.
With excellent processability and improved flow, this product offers the convenience of handling ease with superb performance. Its low temperature ductility allows for ease of use in a range of applications.
Furthermore, this product is non-chlorinated and non-brominated, making it an eco-friendly option for those searching for green solutions. With UL rating of V-0/5VA, you can rest assured about its fire resistance properties.
General | |||||
Form | Resin Pellets | ||||
Feature | Low Temperature Impact | Outdoor Non-Chlorinated | F1 Excellent Processability | ||
Non-Brominated Hi h Im act | |||||
Consumer Electrical | Healthcare | Industria | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.18 1.19 g/cm³ | ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 17 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 16 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion | 1 | UL 746C | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 731 J/m 560 J/m 53 kJ/m² 18 kJ/m² | ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | |||
Instrumented Dart Impact, Total Energy(23 °C) | 67 J | ASTM D3763 | |||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 55 kJ/m² 20 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 | 60 kJ/m² 25 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min | 58 MPa 59 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min | 58 MPa 55 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min | 5.8 % 5 % | ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min | 103 % 100 % | ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min | 2260 MPa 2200 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 95 MPa 88 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2330 MPa 2300 MPa | ASTM D790 ISO 178 |
Ball Indentation Hardness(H358/30) | 95 MPa | ISO 2039-1 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 2.5 mm ≥ 0.8 mm ≥ 1.5 mm | 5VA 5VB HB V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 2.5 mm 3 mm 2 mm 1.5 mm 1 mm | 825 °C 825 °C 825 °C 825 °C 825 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 2.5 mm 3 mm 2 mm 1.5 mm 1 mm | 960 °C 960 °C 960 °C 960 °C 960 °C | IEC 60695-2-12 |
Oxygen Index | 40 % | ISO 4589 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 143 °C 143 °C 144 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 136 °C 123 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C | 7.2e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C | 7.2e-05 1/°C 7.5e-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp=100mm; 0.45 Mpa) | 136 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 124 °C | ISO 75/Ae |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Strength, in Oil(3.2 mm) | 19 kV/mm | IEC 60243-1 |
Relative Permittivity 1.0e+6 Hz 50/60 Hz | 2.7 2.7 | IEC 60250 |
Dissipation Factor 50/60 Hz 1.0e+6 Hz | 4.0E-04 1.0E-02 | IEC 60250 |
Comparative Tracking Index | 175 V | IEC 60112 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 0.8 mm | PLC 2 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI ≥ 1.5 mm ≥ 0.8 mm | PLC 0 PLC 3 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |
Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |