SLX2471T-XH
FOREVER
1 Why FOREVER polycarbonate blend is the priority choice for the UV resisitance in a lont time?
Dongguan Forever Co.,Ltd Medium Viscosity PC Copolymer Blend that is expertly formulated with an enhanced UV stabilization and additional release agent to deliver superior performance. Our V2 rated copolymer blend is perfect for a diverse range of industrial applications such as injection molding, extrusion, and blow molding.
This premium blend of Medium Viscosity PC Copolymer is specifically designed to exceed your expectations. It features an optimal thickness that provides a smooth and effortless flow while maintaining its form factor. With its enhanced UV stabilization formula and added release agent, this copolymer blend is incredibly durable and resistant to impact, heat, and harsh outdoor conditions.
Our Medium Viscosity PC Copolymer Blend is available in transparent and tinted colors, giving it an added aesthetic appeal. Additionally, our copolymer blend is V2 rated, ensuring that it meets the highest safety standards.
Experience the unmatched performance and versatility that our Medium Viscosity PC Copolymer Blend offers. Contact us today to place your order and experience the difference in quality!
General | ||||
Form | Resin Pellets | |||
Feature | Anti-Scratch Color Consistency Outdoor | |||
Automotive Mass Transportation | Electrical Building and Construction Hydrocarbon and Energy | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.2 1.2 g/cm³ | ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.5 - 0.7 % | SABIC Method | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | 1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched | ASTM D256 | |||
23 °C | 820 J/m | |||
-30 °C | 130 J/m | |||
Instrumented Dart Impact, Total Energy(23 °C) | 85 J | ASTM D3763 | ||
Unnotched Izod Impact Strength(unnotched;80*10*3;23 °C 0) | NB kJ/m² | ISO 180/1U | ||
Notched Izod Impact Strength | ISO 180/1A | |||
notched;80*10*3;23 °C 0 | 65 kJ/m² | |||
notched;80*10*3;-30 °C 0 | 10 kJ/m² | |||
Charpy Impact, V-Notched | ISO 179 1eA | |||
23 °C;Edgew;80*10*3;sp=62mm 0 | 65 kJ/m² | |||
-30 °C;Edgew;80*10*3;sp=62mm 0 | 15 kJ/m² | |||
Charpy Impact, Unnotched(23 °C;Edgew;80*10*3;sp=62mm 0) | NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min | 65 MPa 65 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min | 73 MPa 70 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min | 6.4 % 6 % | ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min | > 100 % > 100 % | ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min | 2400 MPa 2300 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 100 MPa 100 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2450 MPa 2450 MPa | ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 1.5 mm) | V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 1 mm | 850 °C 850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 1 mm | 960 °C 900 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 140 °C 140 °C 141 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 126 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C | 7.0E-05 1/°C 7.0E-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C | 7.0E-05 1/°C 7.0E-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test 75°C +/- 2°C 125°C +/- 2°C | PASSES PASSES | IEC 60695-10-2 |
HDT/Af(1.8) | 125 °C | ISO 75/Af |
Relative Temp Index, Elec | 110 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 110 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 110 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm | PLC 0 PLC 2 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1 mm) | PLC 1 | UL 746A |
Optical | Nominal Value | Test Method |
Light Transmission(2.54 mm) | 89 % | ASTM D1003 |
Haze(2.54 mm) | 0.2 % | ASTM D1003 |
Refractive Index | 1.59 | ISO 489 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 300 °C | |
Nozzle Temperature<Injection> | 275 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 265 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 255 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
1 Why FOREVER polycarbonate blend is the priority choice for the UV resisitance in a lont time?
Dongguan Forever Co.,Ltd Medium Viscosity PC Copolymer Blend that is expertly formulated with an enhanced UV stabilization and additional release agent to deliver superior performance. Our V2 rated copolymer blend is perfect for a diverse range of industrial applications such as injection molding, extrusion, and blow molding.
This premium blend of Medium Viscosity PC Copolymer is specifically designed to exceed your expectations. It features an optimal thickness that provides a smooth and effortless flow while maintaining its form factor. With its enhanced UV stabilization formula and added release agent, this copolymer blend is incredibly durable and resistant to impact, heat, and harsh outdoor conditions.
Our Medium Viscosity PC Copolymer Blend is available in transparent and tinted colors, giving it an added aesthetic appeal. Additionally, our copolymer blend is V2 rated, ensuring that it meets the highest safety standards.
Experience the unmatched performance and versatility that our Medium Viscosity PC Copolymer Blend offers. Contact us today to place your order and experience the difference in quality!
General | ||||
Form | Resin Pellets | |||
Feature | Anti-Scratch Color Consistency Outdoor | |||
Automotive Mass Transportation | Electrical Building and Construction Hydrocarbon and Energy | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.2 1.2 g/cm³ | ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.5 - 0.7 % | SABIC Method | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | 1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched | ASTM D256 | |||
23 °C | 820 J/m | |||
-30 °C | 130 J/m | |||
Instrumented Dart Impact, Total Energy(23 °C) | 85 J | ASTM D3763 | ||
Unnotched Izod Impact Strength(unnotched;80*10*3;23 °C 0) | NB kJ/m² | ISO 180/1U | ||
Notched Izod Impact Strength | ISO 180/1A | |||
notched;80*10*3;23 °C 0 | 65 kJ/m² | |||
notched;80*10*3;-30 °C 0 | 10 kJ/m² | |||
Charpy Impact, V-Notched | ISO 179 1eA | |||
23 °C;Edgew;80*10*3;sp=62mm 0 | 65 kJ/m² | |||
-30 °C;Edgew;80*10*3;sp=62mm 0 | 15 kJ/m² | |||
Charpy Impact, Unnotched(23 °C;Edgew;80*10*3;sp=62mm 0) | NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min | 65 MPa 65 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min | 73 MPa 70 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min | 6.4 % 6 % | ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min | > 100 % > 100 % | ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min | 2400 MPa 2300 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 100 MPa 100 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2450 MPa 2450 MPa | ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 1.5 mm) | V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 1 mm | 850 °C 850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 1 mm | 960 °C 900 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 140 °C 140 °C 141 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 126 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C | 7.0E-05 1/°C 7.0E-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C | 7.0E-05 1/°C 7.0E-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test 75°C +/- 2°C 125°C +/- 2°C | PASSES PASSES | IEC 60695-10-2 |
HDT/Af(1.8) | 125 °C | ISO 75/Af |
Relative Temp Index, Elec | 110 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 110 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 110 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm | PLC 0 PLC 2 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1 mm) | PLC 1 | UL 746A |
Optical | Nominal Value | Test Method |
Light Transmission(2.54 mm) | 89 % | ASTM D1003 |
Haze(2.54 mm) | 0.2 % | ASTM D1003 |
Refractive Index | 1.59 | ISO 489 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 300 °C | |
Nozzle Temperature<Injection> | 275 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 265 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 255 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |