LUX9612G-XH
FOREVER
1 What is the MVR and mechanical properties of Forever's diffusion PC pellets?
Product Description | ||||
LUX9612-XH is an injection moldable polycarbonate (PC) grade with a melt volume rate (MVR) of 9 (300°C/1.2kg). It is formulated with a non-brominated, non-chlorinated flame retardant system that meets the UL-94 V0@1.5mm rating. This UV stabilized grade offers high light transmission with a diffusion effect and good color stability during heat exposure. Its thin wall flame retardant (FR) performance makes it an optimal choice for a wide applications. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Non-Brominated Non-Chlorinated Outdoor | |||
Uses | Lighting Applications | Lighting Diffusers | Electronic Displays | |
Physical | Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792; ISO1183 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 |
Mechanical | Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2300 MPa 2230 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Break | ||
50 mm/min | 65.0 MPa 58.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min | 80 % 77 % | ASTM D638 ISO 527-2/50 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2160 MPa 2250 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Break(13 mm/min) | 95.0 MPa | ISO 178 |
Notched Izod Impact 23 °C 23 °C;80*10*3 mm |
400 J/m 40 kJ/m² |
ASTM D256 ISO 180/1A |
Thermal | Value | Test Method |
Deflection Temperature Under Load, Unannealed 1.8 MPa |
123 °C 123 °C |
ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature | 140 °C | ASTM D1525 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
Flame Rating(1.5 mm) | V-0 | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm |
850 °C 850 °C | IEC 60695-2-13 |
Electrical | Value | Test Method |
Comparative Tracking Index[CTI] | PLC 3 | UL 746 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Rear Temperature<Injection> | 260 - 280 °C | |
Middle Temperature<injection> | 270 - 290 °C | |
Nozzle Temperature<Injection> | 270 - 290 °C |
1 What is the MVR and mechanical properties of Forever's diffusion PC pellets?
Product Description | ||||
LUX9612-XH is an injection moldable polycarbonate (PC) grade with a melt volume rate (MVR) of 9 (300°C/1.2kg). It is formulated with a non-brominated, non-chlorinated flame retardant system that meets the UL-94 V0@1.5mm rating. This UV stabilized grade offers high light transmission with a diffusion effect and good color stability during heat exposure. Its thin wall flame retardant (FR) performance makes it an optimal choice for a wide applications. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Non-Brominated Non-Chlorinated Outdoor | |||
Uses | Lighting Applications | Lighting Diffusers | Electronic Displays | |
Physical | Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792; ISO1183 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 |
Mechanical | Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2300 MPa 2230 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Break | ||
50 mm/min | 65.0 MPa 58.0 MPa | ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min | 80 % 77 % | ASTM D638 ISO 527-2/50 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2160 MPa 2250 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Break(13 mm/min) | 95.0 MPa | ISO 178 |
Notched Izod Impact 23 °C 23 °C;80*10*3 mm |
400 J/m 40 kJ/m² |
ASTM D256 ISO 180/1A |
Thermal | Value | Test Method |
Deflection Temperature Under Load, Unannealed 1.8 MPa |
123 °C 123 °C |
ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature | 140 °C | ASTM D1525 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
Flame Rating(1.5 mm) | V-0 | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm |
850 °C 850 °C | IEC 60695-2-13 |
Electrical | Value | Test Method |
Comparative Tracking Index[CTI] | PLC 3 | UL 746 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Rear Temperature<Injection> | 260 - 280 °C | |
Middle Temperature<injection> | 270 - 290 °C | |
Nozzle Temperature<Injection> | 270 - 290 °C |