LUX7436C-XH
FOREVER
1 What is the plastics raw materials for the LED lighting or lamp bulb or profile?
It is light diffusive polycarbonate.Forever PC resins have the features belowing.
LUX7436C-XH Polycarbonate (PC) resin - the perfect solution for your injection molding needs! This incredible material is non-filled, ensuring easy flow and optimal performance during the injection molding process. Made without any chlorine or bromine, LUX7436C-XH is a flame retardant PC with a UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm, providing added safety and peace of mind. Additionally, LUX7436C-XH is UV stabilized with a F1 rating, making it resistant to the damaging effects of weathering. This high-quality resin is also available in diffusion colors, allowing for even greater versatility in your molding projects. Trust LUX74360-XH to provide the durability, safety, and flexibility you need to take your products to the next level.
General | |||||||
Form | Resin | Pellets | |||||
Feature | F1 | Non-Brominated & Non- Non-Chlorinated Chlorinated Flame Retardant | |||||
Automotive Electrical | Lighting Diffusers | Led | |||||
Physical | Value | Test Method | |||||
Density / Specific Gravity |
1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | |||||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | |||||
UV light, water exposure/immersion | F1 | UL 746C | |||||
Mechanical | Value | Test Method | |||||
Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m | ASTM D4812 | |||||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 81 J/m | ASTM D256 |
Notched Izod Impact Strength notched; 23 °C 0 notched;-30 °C 0 |
9 kJ/m² 8 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 7 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
67 MPa 66 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
55 MPa 53 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6 % 6 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
55 % 56 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2520 MPa 2350 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
107 MPa 101 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2450 MPa 2450 MPa |
ASTM D790 ISO 178 |
Thermal | Value | Test Method |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.2 mm |
850 °C 850 °C | IEC 60695-2-13 | |
Glow Wire Flammability Index 3 mm 1.2 mm |
960 °C 960 °C | IEC 60695-2-12 | |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 137 °C 139 °C |
ASTM D1525 ISO 306 ISO 306 | |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
131 °C 120 °C | ASTM D648 | |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | |
HDT/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 120 °C | ISO 75/Ae | |
Relative Temp Index, Elec | 125 °C | UL 746B | |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B | |
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
Electrical | Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.79 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.7E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1.2 mm |
PLC 0 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1.2 mm) | PLC 0 | UL 746A |
Processing | Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
1 What is the plastics raw materials for the LED lighting or lamp bulb or profile?
It is light diffusive polycarbonate.Forever PC resins have the features belowing.
LUX7436C-XH Polycarbonate (PC) resin - the perfect solution for your injection molding needs! This incredible material is non-filled, ensuring easy flow and optimal performance during the injection molding process. Made without any chlorine or bromine, LUX7436C-XH is a flame retardant PC with a UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm, providing added safety and peace of mind. Additionally, LUX7436C-XH is UV stabilized with a F1 rating, making it resistant to the damaging effects of weathering. This high-quality resin is also available in diffusion colors, allowing for even greater versatility in your molding projects. Trust LUX74360-XH to provide the durability, safety, and flexibility you need to take your products to the next level.
General | |||||||
Form | Resin | Pellets | |||||
Feature | F1 | Non-Brominated & Non- Non-Chlorinated Chlorinated Flame Retardant | |||||
Automotive Electrical | Lighting Diffusers | Led | |||||
Physical | Value | Test Method | |||||
Density / Specific Gravity |
1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | |||||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | |||||
UV light, water exposure/immersion | F1 | UL 746C | |||||
Mechanical | Value | Test Method | |||||
Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m | ASTM D4812 | |||||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 81 J/m | ASTM D256 |
Notched Izod Impact Strength notched; 23 °C 0 notched;-30 °C 0 |
9 kJ/m² 8 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 7 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
67 MPa 66 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
55 MPa 53 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6 % 6 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
55 % 56 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2520 MPa 2350 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
107 MPa 101 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2450 MPa 2450 MPa |
ASTM D790 ISO 178 |
Thermal | Value | Test Method |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.2 mm |
850 °C 850 °C | IEC 60695-2-13 | |
Glow Wire Flammability Index 3 mm 1.2 mm |
960 °C 960 °C | IEC 60695-2-12 | |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 137 °C 139 °C |
ASTM D1525 ISO 306 ISO 306 | |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
131 °C 120 °C | ASTM D648 | |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | |
HDT/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 120 °C | ISO 75/Ae | |
Relative Temp Index, Elec | 125 °C | UL 746B | |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B | |
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
Electrical | Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.79 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.7E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1.2 mm |
PLC 0 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1.2 mm) | PLC 0 | UL 746A |
Processing | Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |