100KM NC000-XH is a high viscosity acetal homopolymer with aromatic polyamide resin. It is designed specifically for applications that require low wear in abrasive environments. The common characteristics of 100KM NC000-XH acetal resin include mechanical and physical properties, such as high mechanical strength and stiffness, excellent fatigue and impact resistance, as well as resistance to water, gasoline, lubricants, solvents, and many other neutral chemicals. 100KM NC000-XH acetal resin also has excellent dimensional stability and good electrical insulation properties. They have natural elasticity, self-lubrication, and a variety of colors and special grades to choose from.
General | ||
Form Resin Pellets | ||
Filler Kevlar Fiber | ||
Feature | High Viscosity Abrasion Resistant | Low Friction Homopolymer |
Physical Nominal Value Test Method | ||
Density / Specific Gravity 1.41 g/cm³ ISO 1183 | ||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) 2.0 g/10min ISO 1133 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) 1.7 cm³/10 min ISO 1133 | ||
Molding Shrinkage, Across Flow 1.5 % ISO 294-4 | ||
Molding Shrinkage, Flow 1.8 % ISO 294-4 | ||
Mechanical Nominal Value Test Method | ||
Tensile Modulus 3100 MPa ISO 527-2 | ||
Tensile Stress, Break 65.0 MPa ISO 527-2 | ||
Tensile Strain, Break 15 % ISO 527-2 | ||
Flexural Modulus 3000 MPa ISO 178 | ||
Poisson's Ratio 0.37 No Standard | ||
C harpy Notched Impact Strength ISO 179 1eA | ||
-30 °C 3.5 kJ/m² | ||
23 °C 4.5 kJ/m² | ||
C harpy Unnotched Impact Strength ISO 179 1eU | ||
-30 °C 60 kJ/m² | ||
23 °C 50 kJ/m² |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
160 °C 98.0 °C |
ISO 75-2/B ISO 75-2/A |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
CLTE, Flow
-40 - 23 °C |
1.1E-4 cm/cm/°C 9.4E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse
-40 - 23 °C |
1.0E-4 cm/cm/°C 9.2E-5 cm/cm/°C | ISO 11359-2 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 34 mm/min | ISO 3795 |
FMVSS Flammability | B | FMVSS 302 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time - Desiccant Dryer<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.20 % | |
Processing Temp, Melt<Injection> | 210 - 220 °C | |
Melt Temperature, Optimum<Injection> | 215 °C | |
Mold Temperature<Injection> | 80 - 100 °C | |
Mold Temperature, Optimum<Injection> | 90 °C | |
Holding Pressure<Injection> | 90.0 - 110 MPa | |
Drying Recommended <Injection> | YES | |
Hold Pressure Time<Injection> | 8.00 s/mm | |
Maximum Screw Tangential Speed <Injection> | 12 m/min | |
Drying Temperature<Extrusion> | 75 - 85 °C | |
Drying Time<Extrusion> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Extrusion> | 0.20 % | |
Melt Temperature<Extrusion> | 195 - 205 °C | |
Extrusion Melt Temperature, Optimum<Extrusion> | 200 °C |
100KM NC000-XH is a high viscosity acetal homopolymer with aromatic polyamide resin. It is designed specifically for applications that require low wear in abrasive environments. The common characteristics of 100KM NC000-XH acetal resin include mechanical and physical properties, such as high mechanical strength and stiffness, excellent fatigue and impact resistance, as well as resistance to water, gasoline, lubricants, solvents, and many other neutral chemicals. 100KM NC000-XH acetal resin also has excellent dimensional stability and good electrical insulation properties. They have natural elasticity, self-lubrication, and a variety of colors and special grades to choose from.
General | ||
Form Resin Pellets | ||
Filler Kevlar Fiber | ||
Feature | High Viscosity Abrasion Resistant | Low Friction Homopolymer |
Physical Nominal Value Test Method | ||
Density / Specific Gravity 1.41 g/cm³ ISO 1183 | ||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) 2.0 g/10min ISO 1133 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) 1.7 cm³/10 min ISO 1133 | ||
Molding Shrinkage, Across Flow 1.5 % ISO 294-4 | ||
Molding Shrinkage, Flow 1.8 % ISO 294-4 | ||
Mechanical Nominal Value Test Method | ||
Tensile Modulus 3100 MPa ISO 527-2 | ||
Tensile Stress, Break 65.0 MPa ISO 527-2 | ||
Tensile Strain, Break 15 % ISO 527-2 | ||
Flexural Modulus 3000 MPa ISO 178 | ||
Poisson's Ratio 0.37 No Standard | ||
C harpy Notched Impact Strength ISO 179 1eA | ||
-30 °C 3.5 kJ/m² | ||
23 °C 4.5 kJ/m² | ||
C harpy Unnotched Impact Strength ISO 179 1eU | ||
-30 °C 60 kJ/m² | ||
23 °C 50 kJ/m² |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
160 °C 98.0 °C |
ISO 75-2/B ISO 75-2/A |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
CLTE, Flow
-40 - 23 °C |
1.1E-4 cm/cm/°C 9.4E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse
-40 - 23 °C |
1.0E-4 cm/cm/°C 9.2E-5 cm/cm/°C | ISO 11359-2 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 34 mm/min | ISO 3795 |
FMVSS Flammability | B | FMVSS 302 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time - Desiccant Dryer<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.20 % | |
Processing Temp, Melt<Injection> | 210 - 220 °C | |
Melt Temperature, Optimum<Injection> | 215 °C | |
Mold Temperature<Injection> | 80 - 100 °C | |
Mold Temperature, Optimum<Injection> | 90 °C | |
Holding Pressure<Injection> | 90.0 - 110 MPa | |
Drying Recommended <Injection> | YES | |
Hold Pressure Time<Injection> | 8.00 s/mm | |
Maximum Screw Tangential Speed <Injection> | 12 m/min | |
Drying Temperature<Extrusion> | 75 - 85 °C | |
Drying Time<Extrusion> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Extrusion> | 0.20 % | |
Melt Temperature<Extrusion> | 195 - 205 °C | |
Extrusion Melt Temperature, Optimum<Extrusion> | 200 °C |