3412ECR-XH
FOREVER
3412ECR-XH Polycarbonate (PC) resin, the perfect solution for high stiffness applications.
This grade is made up of 20% glass fiber and is injection moldable, making it a highly versatile product suitable for various manufacturing processes.
Its non-chlorinated and non-brominated flame retardant properties give it an UL-94 V0 rating, ensuring compliance with safety standards. Providing strength and durability, this GF-PC offers excellent physical property retention and is available in several opaque color options, giving you the flexibility you need for your specific application requirements.
General | |||
Form | Resin Pellets | ||
Filler | 20 % Glass Fiber | ||
Feature | High Mechanical Strength Non-Brominated And Rigidity Flame Retardant | Non-Chlorinated | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity |
1.3 1.36 g/cm³ |
ASTM D792 ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7 g/10min | ASTM D1238 | |
Molding Shrinkage, Flow(3.2 mm) | 0.20 - 0.50 % | Internal Method | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.20 - 0.50 % | Internal Method | |
Water Absorption, Saturation(23 °C) | 0.29 % | ISO 62 | |
Moisture Absorption(50 % RH;23 °C) | 0.12 % | ISO 62 | |
Melt Volume Rate, MVR(300 °C;1.2 kg) | 7 cm³/10 min | ISO 1133 | |
Mechanical | Nominal Value | Test Method | |
Tensile Stress, Yield 5 mm/min;type 1 5 mm/min 2 mm/min |
89 MPa 95 MPa 140 MPa |
ASTM D638 ISO 527 ISO 178 | |
Tensile Stress, Break 5 mm/min;type 1 5 mm/min |
86 MPa 90 MPa |
ASTM D638 ISO 527 | |
Tensile Strain, Yield 5 mm/min;type 1 5 mm/min |
3.1 % 2.8 % |
ASTM D638 ISO 527 | |
Tensile Modulus 5 mm/min 1 mm/min |
550 MPa 6000 MPa |
ASTM D638 ISO 527 |
Flexural Stress Yield(1.3 mm/min;50 mm;span) | 156 MPa | ASTM D790 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
4992 MPa 5500 MPa |
ASTM D790 ISO 178 |
Tensile Strain, Break(5 mm/min) | 3.2 % | ISO 527 |
Notched Izod Impact Strength 23 ℃ -30 ℃ 80*10*3;23 ℃ 80*10*3;-30 ℃ |
108 J/m 98 J/m 7 kJ/m² 6 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
Instrumented Impact Total Energy(23 ℃) | 203 cm-kgf | ASTM D3763 |
Unnotched Izod Impact Strength 80*10*3;23 ℃ 80*10*3;-30 ℃ |
35 kJ/m² 35 kJ/m² | ISO 180/1U |
Charpy Impact, V-Notched 80*10*3;23 ℃;sp=62mm 80*10*3;-30 ℃;sp=62mm |
6 kJ/m² 5 kJ/m² | ISO 179/1eA |
Charpy Impact Strength, Unnotched 80*10*3;23 ℃;sp=62mm 80*10*3;-30 ℃;sp=62mm |
40 kJ/m² 40 kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Test Method |
Vicat Softening Point(Rate B/50) | 147 °C | ASTM D1525 |
Heat Deflection Temperature, Unannealed(3.2 mm;1.82 MPa) | 141 °C | ASTM D648 |
CTE, Flow -40 - 40 ℃ 23 - 80 ℃ |
3E-05 1/°C 3E-05 1/°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse -40 - 40 ℃ 23 - 80 ℃ |
7E-05 1/°C 7E-05 1/°C |
ASTM E831 ISO 11359-2 |
Ball Pressure Test(125 ± 2 ℃) | PASSES | IEC 60695-10-2 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
145 °C 146 °C | ISO 306 |
Deflection Temperature 80*10*4;0.45 MPa;BF;flatw;sp= 64 mm 80*10*4;1.8 MPa;flatw;sp= 64 mm;AF |
141 °C 136 °C |
ISO 75/Bf ISO 75/Af |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 130 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Flame Rating 1.5 mm 3 mm |
V-0 5VA | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC-60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 mm) | 825 °C | IEC-60695-2-13 |
Oxygen Index | 40 % | ISO 4589 |
Electrical | Nominal Value | Test Method |
Arc Resistance, Tungsten Electrode(PLC) | Code PLC 7 | ASTM D495 |
Hot Wire Ignition(PLC) | Code PLC 0 | UL 746A |
High Voltage Arc Tracking Rate(PLC) | Code PLC 3 | UL 746A |
High Amp Arc Ignition, HAI, Surface(PLC) | Code PLC 3 | UL 746A |
Comparative Tracking Index(PLC) | Code PLC 3 | UL 746A |
Volume Resistivity | > 1E+15 ohms·cm | IEC 60093 |
Surface Resistivity, ROA | > 1E+15 Ohms | IEC 60093 |
Relative Permittivity 1.0e+6 Hz 60 Hz;50 Hz |
3.3 3.3 | IEC 60250 |
Dissipation Factor 60 Hz;50 Hz 1.0e+6 Hz |
0.02 0.01 | IEC 60250 |
Processing | Nominal Value | |
Drying Temperature | 120 °C | |
Drying Time | 3.0 - 4.0 hr | |
Drying Time, Cumulative | 48 hr | |
Maximum Moisture Content | 0.02 % | |
Melt Temperature | 290 - 310 °C | |
Nozzle Temperature | 280 - 305 °C | |
Front - Zone 3 Temperature | 290 - 310 °C | |
Barrel - Zone 2 Temperature | 275 - 300 °C | |
Barrel - Zone 1 Temperature | 265 - 290 °C | |
Mold Temperature | 70 - 95 °C | |
Back Pressure | 0.3 - 0.7 MPa | |
Screw Speed | 40 - 70 rpm | |
Shot to Cylinder Size | 40 - 60 % | |
Vent Depth | 0.025 - 0.076 mm |
3412ECR-XH Polycarbonate (PC) resin, the perfect solution for high stiffness applications.
This grade is made up of 20% glass fiber and is injection moldable, making it a highly versatile product suitable for various manufacturing processes.
Its non-chlorinated and non-brominated flame retardant properties give it an UL-94 V0 rating, ensuring compliance with safety standards. Providing strength and durability, this GF-PC offers excellent physical property retention and is available in several opaque color options, giving you the flexibility you need for your specific application requirements.
General | |||
Form | Resin Pellets | ||
Filler | 20 % Glass Fiber | ||
Feature | High Mechanical Strength Non-Brominated And Rigidity Flame Retardant | Non-Chlorinated | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity |
1.3 1.36 g/cm³ |
ASTM D792 ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7 g/10min | ASTM D1238 | |
Molding Shrinkage, Flow(3.2 mm) | 0.20 - 0.50 % | Internal Method | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.20 - 0.50 % | Internal Method | |
Water Absorption, Saturation(23 °C) | 0.29 % | ISO 62 | |
Moisture Absorption(50 % RH;23 °C) | 0.12 % | ISO 62 | |
Melt Volume Rate, MVR(300 °C;1.2 kg) | 7 cm³/10 min | ISO 1133 | |
Mechanical | Nominal Value | Test Method | |
Tensile Stress, Yield 5 mm/min;type 1 5 mm/min 2 mm/min |
89 MPa 95 MPa 140 MPa |
ASTM D638 ISO 527 ISO 178 | |
Tensile Stress, Break 5 mm/min;type 1 5 mm/min |
86 MPa 90 MPa |
ASTM D638 ISO 527 | |
Tensile Strain, Yield 5 mm/min;type 1 5 mm/min |
3.1 % 2.8 % |
ASTM D638 ISO 527 | |
Tensile Modulus 5 mm/min 1 mm/min |
550 MPa 6000 MPa |
ASTM D638 ISO 527 |
Flexural Stress Yield(1.3 mm/min;50 mm;span) | 156 MPa | ASTM D790 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
4992 MPa 5500 MPa |
ASTM D790 ISO 178 |
Tensile Strain, Break(5 mm/min) | 3.2 % | ISO 527 |
Notched Izod Impact Strength 23 ℃ -30 ℃ 80*10*3;23 ℃ 80*10*3;-30 ℃ |
108 J/m 98 J/m 7 kJ/m² 6 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
Instrumented Impact Total Energy(23 ℃) | 203 cm-kgf | ASTM D3763 |
Unnotched Izod Impact Strength 80*10*3;23 ℃ 80*10*3;-30 ℃ |
35 kJ/m² 35 kJ/m² | ISO 180/1U |
Charpy Impact, V-Notched 80*10*3;23 ℃;sp=62mm 80*10*3;-30 ℃;sp=62mm |
6 kJ/m² 5 kJ/m² | ISO 179/1eA |
Charpy Impact Strength, Unnotched 80*10*3;23 ℃;sp=62mm 80*10*3;-30 ℃;sp=62mm |
40 kJ/m² 40 kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Test Method |
Vicat Softening Point(Rate B/50) | 147 °C | ASTM D1525 |
Heat Deflection Temperature, Unannealed(3.2 mm;1.82 MPa) | 141 °C | ASTM D648 |
CTE, Flow -40 - 40 ℃ 23 - 80 ℃ |
3E-05 1/°C 3E-05 1/°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse -40 - 40 ℃ 23 - 80 ℃ |
7E-05 1/°C 7E-05 1/°C |
ASTM E831 ISO 11359-2 |
Ball Pressure Test(125 ± 2 ℃) | PASSES | IEC 60695-10-2 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
145 °C 146 °C | ISO 306 |
Deflection Temperature 80*10*4;0.45 MPa;BF;flatw;sp= 64 mm 80*10*4;1.8 MPa;flatw;sp= 64 mm;AF |
141 °C 136 °C |
ISO 75/Bf ISO 75/Af |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 130 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Flame Rating 1.5 mm 3 mm |
V-0 5VA | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC-60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 mm) | 825 °C | IEC-60695-2-13 |
Oxygen Index | 40 % | ISO 4589 |
Electrical | Nominal Value | Test Method |
Arc Resistance, Tungsten Electrode(PLC) | Code PLC 7 | ASTM D495 |
Hot Wire Ignition(PLC) | Code PLC 0 | UL 746A |
High Voltage Arc Tracking Rate(PLC) | Code PLC 3 | UL 746A |
High Amp Arc Ignition, HAI, Surface(PLC) | Code PLC 3 | UL 746A |
Comparative Tracking Index(PLC) | Code PLC 3 | UL 746A |
Volume Resistivity | > 1E+15 ohms·cm | IEC 60093 |
Surface Resistivity, ROA | > 1E+15 Ohms | IEC 60093 |
Relative Permittivity 1.0e+6 Hz 60 Hz;50 Hz |
3.3 3.3 | IEC 60250 |
Dissipation Factor 60 Hz;50 Hz 1.0e+6 Hz |
0.02 0.01 | IEC 60250 |
Processing | Nominal Value | |
Drying Temperature | 120 °C | |
Drying Time | 3.0 - 4.0 hr | |
Drying Time, Cumulative | 48 hr | |
Maximum Moisture Content | 0.02 % | |
Melt Temperature | 290 - 310 °C | |
Nozzle Temperature | 280 - 305 °C | |
Front - Zone 3 Temperature | 290 - 310 °C | |
Barrel - Zone 2 Temperature | 275 - 300 °C | |
Barrel - Zone 1 Temperature | 265 - 290 °C | |
Mold Temperature | 70 - 95 °C | |
Back Pressure | 0.3 - 0.7 MPa | |
Screw Speed | 40 - 70 rpm | |
Shot to Cylinder Size | 40 - 60 % | |
Vent Depth | 0.025 - 0.076 mm |