945DU-XH
FOREVER
Product Description | |||
945DU-XH resin, a high-quality polycarbonate resin that delivers durability and reliability in a range of applications. With a MFR of 10 and MVR of 10, this resin is designed with impact modification that delivers low-temperature ductility, even under harsh conditions. This top-of-the-line product is also UV stabilized and includes mold release. The non-chlorinated, non-brominated flame retardant system ensures UL94 V0, 5VA, 5VB compliance. Available in a variety of opaque colors, 945DU-XH resin is an excellent choice for versatile applications. | |||
General | |||
Form | Resin Pellets | ||
Electronic Displays Electrical Engineering Electrical Household electrics | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 10 g/10min | ASTM D1238 | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 10 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.050 % | ISO 62 | |
Rockwell Hardness, M-Scale | 50 | ASTM D785 | |
Rockwell Hardness, R-Scale | 118 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus 50 mm/min |
2250 MPa 2300 MPa |
ASTM D638 ISO 527-1/1 | |
Tensile Strength, Yield 50 mm/min;Type I |
57.0 MPa 58.0 MPa |
ASTM D638 ISO 527-2/50 | |
Tensile Strength, Break 50 mm/min;Type I |
60.0 MPa 60.0 MPa |
ASTM D638 ISO 527-2/50 | |
Tensile Elongation, Yield 50 mm/min;Type I |
6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 | |
Tensile Elongation, Break 50 mm/min;Type I |
100 % 95 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2250 MPa 2300 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 90.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 95.0 MPa | ASTM D790 |
Charpy Notched Impact Strength -40 °C;80 -30 °C;80 23 °C;80 |
56 kJ/m² 58 kJ/m² 64 kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength(23 °C;80) | No Break | ISO 179/1eU |
Notched Izod Impact -40 °C -30 °C 23 °C -40 °C;80*10*3 mm -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
520 J/m 600 J/m 700 J/m 50 kJ/m² 55 kJ/m² 65 kJ/m² |
ASTM D256 ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A ISO 180/1A |
Unnotched Izod Impact(23 °C) | No Break | ASTM D4812;ISO 180/1U |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa;3.2 mm | 134 °C | ASTM D648 |
1.8 MPa;3.2 mm | 120 °C | ASTM D648 |
80*10*4 mm;0.45 MPa;4 mm;64 mm;Span | 134 °C | ISO 75-2/Bf |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 120 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 145 °C
143 °C | ASTM D1525;ISO 306/B120 ISO 306/B50 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow -40 - 40 °C 23 - 80 °C |
7.0E-5 cm/cm/°C 7.2E-5 cm/cm/°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse -40 - 40 °C 23 - 80 °C |
7.1E-5 cm/cm/°C 7.5E-5 cm/cm/°C |
ASTM E831 ISO 11359-2 |
Thermal Conductivity |
0.27 W/m-K |
ASTM C177 |
0.96 W/m-K | ASTM E1530 | |
Flame Rating, Testing by SABIC 1.2 mm 2 mm 3 mm |
V-0 5VB 5VA | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 mm) | 875 °C | IEC 60695-2-13 |
Product Description | |||
945DU-XH resin, a high-quality polycarbonate resin that delivers durability and reliability in a range of applications. With a MFR of 10 and MVR of 10, this resin is designed with impact modification that delivers low-temperature ductility, even under harsh conditions. This top-of-the-line product is also UV stabilized and includes mold release. The non-chlorinated, non-brominated flame retardant system ensures UL94 V0, 5VA, 5VB compliance. Available in a variety of opaque colors, 945DU-XH resin is an excellent choice for versatile applications. | |||
General | |||
Form | Resin Pellets | ||
Electronic Displays Electrical Engineering Electrical Household electrics | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 10 g/10min | ASTM D1238 | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 10 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.050 % | ISO 62 | |
Rockwell Hardness, M-Scale | 50 | ASTM D785 | |
Rockwell Hardness, R-Scale | 118 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus 50 mm/min |
2250 MPa 2300 MPa |
ASTM D638 ISO 527-1/1 | |
Tensile Strength, Yield 50 mm/min;Type I |
57.0 MPa 58.0 MPa |
ASTM D638 ISO 527-2/50 | |
Tensile Strength, Break 50 mm/min;Type I |
60.0 MPa 60.0 MPa |
ASTM D638 ISO 527-2/50 | |
Tensile Elongation, Yield 50 mm/min;Type I |
6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 | |
Tensile Elongation, Break 50 mm/min;Type I |
100 % 95 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2250 MPa 2300 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 90.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 95.0 MPa | ASTM D790 |
Charpy Notched Impact Strength -40 °C;80 -30 °C;80 23 °C;80 |
56 kJ/m² 58 kJ/m² 64 kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength(23 °C;80) | No Break | ISO 179/1eU |
Notched Izod Impact -40 °C -30 °C 23 °C -40 °C;80*10*3 mm -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
520 J/m 600 J/m 700 J/m 50 kJ/m² 55 kJ/m² 65 kJ/m² |
ASTM D256 ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A ISO 180/1A |
Unnotched Izod Impact(23 °C) | No Break | ASTM D4812;ISO 180/1U |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa;3.2 mm | 134 °C | ASTM D648 |
1.8 MPa;3.2 mm | 120 °C | ASTM D648 |
80*10*4 mm;0.45 MPa;4 mm;64 mm;Span | 134 °C | ISO 75-2/Bf |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 120 °C | ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 145 °C
143 °C | ASTM D1525;ISO 306/B120 ISO 306/B50 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow -40 - 40 °C 23 - 80 °C |
7.0E-5 cm/cm/°C 7.2E-5 cm/cm/°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse -40 - 40 °C 23 - 80 °C |
7.1E-5 cm/cm/°C 7.5E-5 cm/cm/°C |
ASTM E831 ISO 11359-2 |
Thermal Conductivity |
0.27 W/m-K |
ASTM C177 |
0.96 W/m-K | ASTM E1530 | |
Flame Rating, Testing by SABIC 1.2 mm 2 mm 3 mm |
V-0 5VB 5VA | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 mm) | 875 °C | IEC 60695-2-13 |